鞣酸模板交联壳聚糖/凹凸棒石黏土复合树脂的制备与表征

以鞣酸为模板,采用乳化交联法制备了鞣酸模板交联壳聚糖/凹土复合树脂(TA-CS/ATP)。采用扫描电子显微镜(SEM)和傅里叶变换红外光谱仪(FT-IR)分别对树脂形貌和结构进行表征,用孔参数对其性能进行评价。考察了模板分子的加入量对树脂吸附容量的影响,并根据洗脱率对模板洗脱液进行选择。结果表明:与非模板树脂相比,当壳聚糖与模板的质量比为1.00∶0.05时,树脂的孔度值和膨胀率分别从48%和57.41%提高到79%和87.05%,吸附容量由314.7 mg/g增加到445.7 mg/g。树脂的再生性能研究表明,凹土和模板分子的加入,使树脂在酸中的失重率从18.45%降低到6.18%,且树脂经过4次再生使用仍然具有较高的吸附容量。     

绿色缓蚀阻垢剂聚环氧琥珀酸的中试生产研究

在复合型催化剂存在下,以马来酸酐为原料,通过一步法对聚环氧琥珀酸进行了中试试验,经红外光谱表征测试证明产物与聚环氧琥珀酸含有相同的基团。经多次工业试验,收率可达90%以上,聚环氧琥珀酸质量含量为30%。     

石脑油加氢精制催化剂LY-2010的工业应用

开发了一种石脑油加氢精制催化剂LY-2010,以中国石油兰州石化公司直馏石脑油为原料,在360mL绝热评价装置上对LY-2010与国内参比剂进行了对比评价。结果表明,在重整预加氢反应器入口温度较使用参比剂时低10℃的条件下,LY-2010催化剂的加氢性能依然略优于参比剂。LY-2010催化剂在中国石油辽阳石化公司1.4 Mt/a连续重整装置首次工业应用,一次开车成功,在入口温度274℃、反应压力2.2 MPa、体积空速5.0h-1的条件下,加氢石脑油产品硫、氮质量分数均小于0.5μg/g,完全满足重整装置进料指标的要求。     

平凉钙基膨润土干法钠化工艺研究

采用干法工艺,对甘肃平凉膨润土进行钠化改性,分别从不同钠化剂(碳酸钠、氯化钠、氢氧化钠)的选择和配比、钠化高混时间、自然放置时间等因素对钠化土性能的影响进行了研究.用FT IR和XRD对钠化土进行分析,结果表明,钠化土在不改变原土结构的同时发生了阳离子交换,层间距明显增大.     

壳聚糖/改性凹土复合树脂的制备及其缓释性能研究

以壳聚糖和改性凹土为原料,采用氢氧化钠固化,戊二醛交联的方法制备了壳聚糖/改性凹土复合树脂微球,分别采用FT-IR和TG对树脂进行结构表征。以阿司匹林为模型药物,考察了树脂的缓释性能,并对最优条件下树脂释放药物的曲线进行了动力学模型拟合。研究结果表明,CS/O-ATP树脂的吸附性能和缓释性能最佳,当戊二醛的加入量为6mL时,其载药量和包封率分别为12.2%和39.88%,且缓释效果较好。CS/O-ATP树脂的药物释放规律复合Higuchi方程,表明该树脂可以作为长效药物的缓释载体。     

KOH—K2CO3活化废弃焦粉制备活性炭的研究

采用KOH-K2CO3复合活化剂,对废弃焦粉在不同活化剂与焦粉比、活化温度、活化时间、粒径大小等工艺条件下进行正交实验,得出影响制备焦粉活性炭的主次因素为活化温度、活化剂与焦粉比、粒径大小、活化时间;制备焦粉活性炭的最优方案为活化剂与焦粉比6:1,活化温度850℃,活化时间100min,粒径大小<0.05mm.制备的焦粉活性炭其比表面积为303m#/g,总孔、中孔、微孔容积分别为0.392 4cm3/g、0.215 9cm3/g、0.143 1cm3/g.焦粉活性炭有利于吸附相对分子量较大的物质.     

Preparation and properties of PAn/ATTP/PE conductive composites

Polyaniline/Attapugite/PE（PAn-ATTP/PE）composites containing particles with core-shell structure were obtained via the two-step blending processs. The experimental condition is as follows： Organo-attapulgite and PAn was obtained by modifying attapulgite with laury benzenesulfonic acid sodium salt and, then added to PE. The electrical conductivity, structure and properties of the composites were studied. Under the function of shear stress, core-shell structure particles with ATTP as the core and PAn as the shell were formed in the composites. The structure of PAn-ATTP/PE composites were characterized by FTIR,XRD,SEM, etc, respectively. The effects of concentration of doping agent on the conductivity and mechanical property of the composites were investigated. The mechanical properties and impact fracture surface of the ternary composites were studied by means of the tensile tester, SEM, etc. The results show that polyaniline encapsulated ATTP enhances the strength of the PE. And the conductivity of PAn-ATTP/PE composites of is improved effectively when polyaniline encapsulated ATTP is added. The composite have good conductivity when 10% polyaniline encapsulated ATTP is added.     

石墨烯类润滑添加剂的研究进展

石墨烯具有良好的减摩抗磨性能,对其表面化学改性和纳米颗粒修饰可以提高其在润滑油中的性能。氮化硼、二硫化钨、二硫化钼等材料具有与石墨烯类似的二维结构,均是良好的固体润滑剂。综述了石墨烯类润滑油添加剂在摩擦学中的应用。     

硅藻土复合磁性壳聚糖对铬(Ⅵ)离子吸附性能

以硅藻土、壳聚糖和Fe3O4为主要原料,制得硅藻土复合磁性壳聚糖材料DE/M-CS。分别考察了Fe3O4和壳聚糖与硅藻土质量比、pH、吸附时间、吸附温度等对铬(Ⅵ)离子吸附性能的影响。结果表明,低温有利于吸附,当m(Fe3O4)∶m(壳聚糖)∶m(硅藻土)=1∶1∶1、溶液pH为3、温度为15℃、吸附时间为6 h、达到吸附平衡时,DE/M-CS对铬(Ⅵ)离子吸附量为47.8 mg/g;吸附符合Langmuir等温模型,符合准二级动力学模型,吸附为放热反应。在吸附材料吸附饱和后,可以采用0.1 mol/L氢氧化钠溶液进行再生利用,重复使用4次后,DE/M-CS对铬(Ⅵ)离子吸附量为37.8 mg/g。     

一步法合成聚环氧琥珀酸实验研究

以马来酸酐为原料,使用复合型催化剂,通过一步法合成了聚环氧琥珀酸,并用正交实验设计法对聚环氧琥珀酸合成过程的工艺条件进行了优化.经红外光谱表征和1HNMR核磁测试,证明产物与聚环氧琥珀酸含有相同的基团,经阻垢实验测试,产物具有较强的阻垢性能.