采用真空电弧熔炼和热处理方法制备了La1-xCexNi3.54Co0.78Mn0.35Al0.32(x=0.1,0.2,0.3,0.4,0.5,0.6)贮氢合金.X射线衍射(XRD)分析表明,合金含有单一CaCu5型六方结构相.电化学性能测试表明,随着x的增加,合金的最大放电容量从348.1mAh/g(x=0.1)单调地减小到310.1 mAh/g(x=0.6);HRD1200先从28.6%(x=0.1)增加到65.4%(x=0.5)然后降低到60.1%(x=0.6),归因于合金表面的电催化活性和合金体内氢原子扩散速率均随x的增大先增大后减小. 相似文献
2.
3.
4.
5.
采用感应熔炼和热处理的方法制备La0.7Ce0.3Ni3.75Mn0.35Al0.15Cu0.75?xFex(x=0~0.20)合金,并研究合金的相结构和电化学储氢性能。全部合金均为单一的具有CaCu5结构的LaNi5相,LaNi5相的晶格常数a和晶胞体积随着x值的增加而增大。最大放电容量随着x值的增加从319.0mA·h/g(x=0)降低到291.9mA·h/g(x=0.20)。在1200mA/g的电流密度下HRD值从53.1%(x=0)降低到44.2%(x=0.20)。合金电极的循环稳定性随着x值的增加而增强,这主要归因于合金抗粉化能力的增强。 相似文献
6.
7.
采用恒电位法、EIS分析及双电极系统对La0.8Mg0.2(Ni2.7Co0.6Al0.1Mn0.1)x(x=0.9~1.10)系列合金进行电化学性能分析。结果表明,x=1.05的合金具有较好的自放电性能(CR=97.3%),而x=1.10的合金有较高的电化学容量(369 mAh.g-1)。合金电极的电化学阻抗谱(EIS)表明,随着化学计量比x的增大,合金电极的电荷迁移电阻先减小后增大,动力学性能先增强后减弱。线性极化测试表明,随着化学计量比x的增大,合金电极表面的电化学反应速率先增大后减小。通过合金电极阳极电流对时间响应的半对数曲线计算的氢扩散系数D随着化学计量比x的增大先增大后降低,说明合金内部的氢扩散能力先增强后降低。 相似文献
8.
Phase structure and electrochemical characteristics of Co-free La0.7Ce0.3(Ni3.65Cu0.75Mn0.35Al0.15(Fe0.43B0.57)0.10)x (0.90≤x≤1.10) al-loys were investigated. When x was 0.90, the alloy was composed of LaNi5, La3Ni13B2 and Ce2Ni7 phases. The Ce2Ni7 phase disappeared, and the abundant of La3Ni13B2 phase decreased when x increased to 0.95. When x was 1.00 or higher the alloys consisted of LaNi5 phase. The lat-tice parameter a and the cell volume V of the LaNi5 phase decreased, and the c/a ratio of the LaNi5 phase increased with x value increasing. Maximum discharge capacity of the alloy electrodes first increased and then decreased with x value increasing from 0.90 to 1.10, and the highest value was obtained when x was 1.00. High-rate dischargeability at the discharge current density of 1200 mA/g increased from 50.7% (x= 0.90) to 64.1% (x=1.10). Both the charge-transfer reaction at the electrode/electrolyte interface and the hydrogen diffusion in the alloy were responsible for the high-rate dischargeability. Cycling capacity retention rate at 100th cycle (S100) gradually increased from 77.3% (x= 0.90) to 84.6% (x=1.10), which resulted from the increase in Ni content and the c/a ratio of the LaNi5 phase with x value increasing. 相似文献
9.
氢气作为一种清洁能源,被认为是化石能源最理想的替代者。安全、高效且稳定的储氢材料的开发是当前氢能源应用研究中面临的最大挑战之一。氨硼烷(NH3BH3,AB)因其较高的储氢密度(146 g·L-1,质量分数为19.6%)、安全无毒及高化学稳定性等特性成为一种重要的化学固态储氢材料。氨硼烷水解制氢反应条件温和,但需要在合适的催化剂存在的条件下进行。通过调节催化剂的活性组分、颗粒尺寸、活性组分的分散度、电子结构等,可显著提高氨硼烷水解产氢速率。综述了近年来氨硼烷水解制氢反应中镍基催化剂的研究进展,重点概述了镍单质、镍化合物以及镍合金催化剂在氨硼烷水解产氢中的应用,阐述了氨硼烷水解产氢反应机理,展望了氨硼烷水解产氢的发展趋势以及面临的挑战。 相似文献