热酸浸出-铁矾法炼锌工艺中富集锗的研究

进行了"热酸浸出-铁矾法炼锌工艺中锗和银的富集和回收"的实验室扩大试验,在10个循环试验中,工艺流程畅通,以黄钾铁矾沉铁代替通常的钠或铵铁矾沉铁使锗在矾渣中的损失减少到5.0%以下,锗和银均富集于高酸浸出渣中,其品位分别为0.0325%和0.162%.     

硫酸锌溶液低温锑盐除钴研究

硫酸锌溶液锑盐净化通常在高于75℃的温度下进行。近年来，低温（55－66℃）下深度净化除钴工艺研究取成功。从热力学、动力学角度对锑盐净化除钴机理进行分析，可以阐明其适应性，及证实在较低温度下净化除钴的可行性，为工业生产提供理论依据。热力学分析结果表明，在温度高于50℃时，锑盐除钴可以达到很低的限度；温度从50℃升到75℃，钴析出超电压的变化主要来源于CaSb,CoSb2的形成；而因氢在锑上具有较高超电压（0．5－0．7V），则抑制了氢的析出。动力学分析结果表明，在温度高于50℃后，锑盐除钴处于阴极过程的扩散控制区域，温度升高对反应速度影响不大，相反却加剧了Zn∧2＋的解，因而抑制了钴的析出。提出了锑盐除钴时应注意的几个问题。     

焊接与节能

<正> 一、前言电焊机是耗能较多的电气设备,我国目前有焊接设备约70万台,每年将消耗电能7.5亿kWh,有些机械厂要占总用电量的20～25％,而造船厂的船台车间、客车厂的车体车间等甚     

Concentrating Ge in zinc hydrometallurgical process with hot acid leaching-halotrichite method

1　INTRODUCTIONInthezincconcentratesfromHuidongLead zincMinelocatedinsouth westofChina ,therearerichraremetalssuchasGewhichhasverywideapplica tionsandhighvalue .However ,Gewaslargelywast edbecauseitwasdispersedinalotofresidues(halotrichiteresidue ,Ge Feresidueandhighacidleachedresidue)intheconventionalzinchydrometal lurgicalprocessforthezincconcentrates[1] .InordertoconcentrateandrecoverGe ,anovelhydrometal lurgicalprocess ,ie ,thehotacidleaching halotrichitemethodofzinchasbeendevelope…     

窑法磷酸中铁、铅、砷的深度净化

对沉淀法深度净化窑法磷酸中的铁、铅和砷进行了研究。理论计算表明,采用亚铁氰化铁沉淀法除铁,可以将w(Fe)降低至≤1 mg/kg;采用硫化物沉淀法除铅、除砷,当净化液中c(S)≥9.46×10-5mol/L时,可以将w(Pb)和w(As)分别降至10 mg/kg、1 mg/kg。实验结果表明,当亚铁氰化钠加入量为理论量、反应温度为50℃时,w(Fe)降至0.001 9%(折合w(H3PO4)85%磷酸中);当五硫化二磷加入量为理论量4.6倍、反应温度为20~30℃以及反应时间为0.5 h时,w(Pb)和w(As)分别降至7.5 mg/kg、0.15 mg/kg(折合w(H3PO4)85%磷酸中)。上述净化指标均达到了工业级磷酸国家标准(GB/T 2091—2008)的要求。     

铜掺杂TiO_2纳米管阵列的制备与光催化还原性能

以阳极氧化法制得的TiO2纳米管阵列为前驱体,用浸渍法制备了不同铜掺杂量的TiO2纳米管阵列。采用场发射扫描电镜(FE-SEM)、X射线衍射(XRD)、X光电子能谱(XPS)、荧光光谱(PL)对样品进行表征。以Cr6+水溶液为目标污染物,对比不同铜掺杂量TiO2纳米管阵列的光电催化还原效果。结果表明,掺杂前后TiO2纳米管阵列在形貌上没有明显变化;掺杂的铜是以Cu2+的形态存在;掺铜后TiO2纳米管阵列还原效果优于掺铜前;低剂量铜掺杂的TiO2纳米管阵列的还原效果优于高剂量铜掺杂的TiO2纳米管阵列。     

双极膜电渗析用于分子筛清洁化离子交换的研究

In view of the problems of large amount of discharged waste water and serious pollution in the existing technology of removing sodium from molecular sieves, the research introduces the bipolar membrane electrodialysis into the process of removing sodium from molecular sieves, and proposes a novel method of cleanly removing sodium from molecular sieves. The results show that the technology of removing sodium ions in the molecular sieves with an indirect electrodialysis process is feasible, and can recover NaOH solution, bipolar membrane electrodialysis is especially suitable for the USY, ZSM-5 and Beta molecular sieves with high acid-resistance, the physicochemical properties and catalytic performance of the prepared molecular sieves are roughly equivalent with those of the ammonium exchange method. As compared with the ammonium exchange method, the process is clean and environment-friendly, consumes less water, and does not discharge waste water, thereby exhibits a rosy prospect of industrial application.     

湿法炼锌工艺中溶液澄清方面存在的问题

湿法炼锌生产中Fe,Al,Si的行为对溶液澄清有重要影响，通过理论分析并结合生产实践，阐述了湿法炼锌工艺流程中溶液澄清方面存在的问题，同时提出了改进措施。     

盐酸氧化酸浸-亚硫酸钠浸出法处理银精矿氧化焙砂的研究

湿法炼锌过程中产出的铅银渣经硫化浮选得到的银精矿 ,通过氧化焙烧产出含银达± 1 .0 %的富银焙砂。研究了采用盐酸氧化酸浸预处理该富银焙砂以分离锌、铜等 ,同时使银转化为氯化银 ,再用亚硫酸钠碱性络合浸出转化渣回收银的工艺。考查了盐酸氧化酸浸过程中银的分散情况 ,结果表明 ,该过程中银的浸出率平均为 2 .7% ;采用了单因素条件试验研究方法 ,在试验的最佳条件下 ,富银焙砂经盐酸氧化酸浸后亚硫酸钠络合浸银 ,银的浸出率达 90 %以上 ,浸银液未经净化 ,直接用水合肼还原可得含量为 96 %以上的银粉。     

低品位复杂红土镍矿微波干燥及矿相分析

研究了在碳化硅辅助吸波作用下,低品位红土镍矿在微波场中的干燥过程.采用热重分析(DTG)、X射线衍射(XRD)和傅里叶变换红外光谱(FT-IR)分析考察了添加不同质量分数碳化硅对失重率和产物物相的影响.结果表明:碳化硅与红土矿配比R为2.2:1时,微波干燥处理低镍、铁品位红土矿30min,既可快速脱除矿物绝大部分表面吸附水和部分结晶水;通过控制碳化硅的比例还可以避免过热现象.微波能够改变红土矿的微观结构,促进矿物的分解.进一步的氢还原实验表明,微波干燥有利于红土矿中镍和铁氧化物的还原,其还原率高于常规干燥.