采用水冷铜坩埚真空感应熔炼炉制备了Ti-47Al-1.2Ce合金.通过XRD,SEM,EMPA和TEM等测试方法,研究了Ce对TiAl基合金显微组织的影响以及富稀土相的形貌.实验结果表明,铸态Ti-47Al-1.2Ce合金由等轴晶组成,富稀土相主要以椭球形存在于晶内和以网状存在于晶界;稀土元素的加入,可以减小TiAl相的单胞体积,细化合金晶粒尺寸和层片间距.     

Ti-22Al-25Nb合金ISM熔炼过程中的成分控制

采用X荧光光谱(XRF)分析水冷铜坩埚真空感应炉熔炼(ISM)加入和不加入稀土Y的Ti-22Al-25Nb合金铸锭成分,分析结果表明,在保证获得成分均匀的合金铸锭的情况下,Al的挥发烧损在28.94%～33.88%之间;加入at为0.5%～1%Y,Y的挥发烧损在w为17.20%～34.26%;采取提高熔化温度降低保温时间的措施可以降低Al的挥发烧损.     

Recent developments in engineering γ—TiAl intermetallics

γ-TiAl based alloys are rapidly being developed for elevated temperature applications,due to their high strength,light mass and good oxidation resistance.However,th disadvantages of TiAl based alloys are low ductility and toughness at room temperature,and poor workability.Grain refinement is one of the most effective ways for improving room temperature tensile properties and hot workability of ordered TiAl based alloys.At present,the majority of research works have focused on alloy modifications through compositional controls,alloying additions,thermo-mechanical processing and production techniques.This article discusses the research status of TiAl based alloys in the aras of microstructure,alloying,processing and applications.     

安全管理 打造石化企业核心竞争力——2014中国国际石油化工大会专题报道之五

在新形势下如何看待安全？在石化企业看来,这个问题的重要性并没有因为多变复杂的形势、多重的压力而被忽视,追求可持续发展需要安全。在中国石油和化学工业联合会与天津市人民政府联合主办的2014中国国际石油化工大会上,一场以“石化企业的可持续发展之道”为主题的安全管理专业研讨会吸引了众多目光。     

双相区热处理对A508-3钢的冲击性能及断口形貌的影响

采用Charpy（V型缺口）试样对A508-3钢调质处理试样和双相区热处理试样在-196～20℃温度范围内进行示波冲击试验,用扫描电镜对冲击断口形貌进行观察,研究了冲击温度对两种热处理制度下该钢的冲击性能和断口形貌的影响。调质处理试样随着温度的降低,其冲击功和侧膨胀量急剧降低,断裂方式从韧脆混合断裂变为脆性断裂,断口形貌中纤维区和剪切唇面积不断减少,放射区面积相应增大;双相区热处理试样在-20～-100℃冲击时,其冲击功和侧膨胀量改变甚小,断裂方式为全韧性断裂,断口形貌全部为剪切唇和纤维区组成,随着温度的继续降低,冲击功和侧膨胀量开始急剧下降,断裂方式变为韧脆混合断裂,断口形貌出现放射区,放射区微观特征为准解理。与调质处理相比,该钢经双相区热处理后冲击性能大大提高,韧脆转变温度急剧降低。     

Analysis of electron structure of γ/α2 phase boundaries in ternary TiAl intermetallics

The electron structure of γ/α2 phase boundaries in lamellar colonies in Ti-47Al-2M（M=Nb, Cr, V） （mole fraction, %） alloys was theoretically investigated by Empirical Electron Theory of Solid and Molecules （EET） and the bond-length-difference （BLD） method. Average-Atom-Model was employed to calculate valence electron structure of TiAI intermetallics containing site substitution elements. On this basis, the boundary condition of electron movement was employed in the improved Thomas-Fermi-Dirac （TFD） theory to decide the continuity of the electron density of the lamellar colonies interface and it is found that of γ/α2 interface is continuous（△ρ〈10%）. Furthermore, it is found that adding alloying elements （including Nb, Cr, and V） can improve the electron density （ρ） of ）γ/α2 interfaces, and decrease the electron density difference（△ρ） of γ/α2 interfaces. Adding V element decreasing △ρ is more remarkable than other site substitution elements. According to electron structure study of γ/α2 interfaces in Ti-47Al-2M alloys, the added elements improve mechanical properties of the alloy in the following order： V〉Cr〉Nb.     

音频大地电磁法在贵州石阡青阳地区锰矿中的应用

通过在贵州石阡青阳地区选择锰矿勘查程度较高、周缘含锰岩系出露较好、深部埋藏较为完整的矿区,按照200米点距布置测线开展音频大地电磁(AMT)测量工作,获取测区2.5千米深部电性结构模型。参考研究区及邻区已有地质地球物理成果及钻井等资料,遵循"大塘坡"式锰矿赋存的地层构造特征,对电性结构开展地质地球物理综合解释。大地电磁勘探成果查明了成锰槽盆的深部结构形态及含锰岩系的大致空间位置。     

氧和氮对TiAl合金精密热成形显微组织和力学性能的影响

TiAl合金因其密度低、比强度高,在700~900 ℃具有良好的耐氧化性、抗蠕变和疲劳性能等优点,是最具应用前景的耐高温结构材料。氧、氮原子在TiAl合金真空熔炼、精密铸造、粉末冶金和增材制造等精密热成形中的变化,对组织转变和性能的影响不可忽视,氧、氮原子使合金室温塑性降低,是限制其工程化应用的关键因素之一。介绍了氧、氮原子对TiAl合金在精密热成形过程中显微组织和力学性能的影响,并进一步阐述了热成形工艺参数与TiAl合金氧和氮含量之间的关系。     

TiAl合金的热加工、组织和性能

采用水冷铜坩埚感应熔炼技术制备了高质量的Ti-43Al-9V-0.3Y合金铸锭,该合金铸态组织为近层片组织结构,层片团簇的体积分数为85%左右,大小约为80μm,块状β和γ相位于层片团簇边界。层片结构中除了γ和α2相外,还存在少量的β相析出物。Ti-43Al-9V-0.3Y合金具有良好的热加工性能,通过包套锻造和包套轧制技术,成功制备了大尺寸TiAl合金锻饼和国内最大尺寸TiAl合金板材,其尺寸分别为260mm×24mm和500mm×300mm。经热变形后,Ti-43Al-9V-0.3Y合金的显微组织明显细化,力学性能得到了显著提高。     

热机械处理对Ti-45Al-5Nb-0.3Y合金的显微组织与力学性能的影响

包套锻造Ti-45Al-5Nb-0.3Y合金由大量细小的动态再结晶等轴γ晶粒(晶粒尺寸可达1-2 μm),弯曲或破碎的层片和少量的残余平直层片组成,变形组织含有人量位错及少量变形孪晶.锻态试样抗拉强度(σb),延伸率(δ)分别达到708.1 MPa和0.95%.再通过不同的热处理分别得到晶粒细小的双态组织、近层片组织和全层片组织.经1320 ℃/30 min炉冷后得到双态组织,层片晶粒尺寸(d1)约为20 μm,层片体积分数(ψ1)约为60%,具有最高的δ,约为1-9%,σb约为658.9 MPa,为穿晶和沿晶混合断裂;经1340℃/30 min炉冷后得到近层片组织,dI约为60 gm,ψ1约为95%,O'b约为690.2 MPa,δ约为1.75%,上要为穿晶(层片)断裂;经1370℃/15 min炉冷后得到细小全层片组织(d1约为40 μm),具有最高的σb,约为715.1 MPa,5约为1.51%,为穿晶断裂.