贮氢合金在高温下会表现出与常温不同的电化学特性,以La0.75Mg0.25Ni3.5Si0.10合金为研究对象,采用交流阻抗谱和电位阶跃方法,对其高温使用环境下(30~70℃)的高倍率放电特性和动力学性能进行了深入的研究。研究结果表明合金的动力学性能是由电化学反应与氢的扩散共同控制的,合金的电荷传递电阻随温度升高而减小,高温有助于电极表面电化学反应速度的提高;但对于La0.75Mg0.25Ni3.5Si0.10合金存在最佳氢扩散温度,当温度高于其最佳温度时,由于释氢等副反应的进行,以及氧化腐蚀反应的加剧等,使合金的扩散系数反而减小;在合金表面电化学反应速度与氢扩散系数共同作用下,La0.75Mg0.25Ni3.5Si0.10合金高倍率放电性能在45℃时最优异,当温度高于45℃时反而降低。 相似文献
3.
4.
6.
7.
La0.75Mg0.25Ni3.5–xCo0.2Alx (x=0–0.09) hydrogen storage alloys were prepared by induction melting and effect of Al substitution for Ni on phase constitution and electrochemical property was investigated.With the substitution of Al for Ni,LaNi5 and LaNi2 phases occurred and (La,Mg)2(Ni,Co,Al)7 phase with hexagonal Ce2Ni7-type structure replaced (La,Mg)2(Ni,Co)7 phase.The cell volumes of LaNi5 and (La,Mg)2(Ni,Co,Al)7 main phases increased with increasing Al content.Some electrochemical properties and kinetic parameters of the alloys,including discharge capacity,high rate discharge ability (HRD),loss angle (ψ),exchange current density (I0) and limiting current density (IL),decreased with increasing amount of substitution of Al for Ni.Substitution of Al for Ni could be favorable for positive shift in corrosion potential of the alloy electrode,and prolonged cyclic lifetime of La0.75Mg0.25Ni3.5–xCo0.2Alx (x=0–0.09) alloy electrodes. 相似文献
8.
9.
研究了快淬处理对AB2型Laves相电极合金循环稳定性的影响,用XRD和SEM分析了铸态及快淬态合金的相结构,并观察了合金的微观组织形貌。结果表明,快淬对AB2型贮氢合金循环稳定性的影响与合金的成分密切相关。快淬对Ti基电极合金的循环寿命有所提高,但不显著;对Ti—Zr基合金,随淬速增加,合金的循环稳定性急剧增加。快淬使AB2型电极合金循环寿命发生变化的根本原因是合金中形成了不同量的非晶相。 相似文献
10.