Effect of temperature on mechanical behavior of AZ31 magnesium alloy

Strain rate sensitivity and tension/compression asymmetry of AZ31 magnesium alloy at different temperatures and strainrates were investigated.Both of mechanical behaviors are temperature dependent.Strain rate sensitivity increases with increasingtemperature.Thermally activated slip is the source of strain rate sensitivity.At the temperature below or near 373 K,strain ratesensitivity is very little.Tension/compression asymmetry in yielding decreases with increasing temperature.Twinning is the reasonof tension/compression asymmetry.At the temperature above or near 573 K,the material shows little tension/compressionasymmetry of the flow stress.     

绝热剪切带内微孔洞演化规律研究

为深入了解绝热剪切带内微孔洞的演化规律,进而揭示高应变率加载条件下绝热剪切破坏的特殊规律,本文对D35钢进行了约束爆破实验,爆破后回收圆筒的微观观察表明,绝热剪切破坏要经过绝热剪切带内微孔洞形核、长大和相互联接形成裂纹等一系列演化过程.在Guduru P等人的测试结果和Li Shaofan等人数值仿真结果基础上,通过简化(剪切带内的温度分布为由剪切带中心向边缘线性降低,并最终降至与基体温度相同; 微孔洞的形核、长大受温度控制,长大速度随温度呈指数规律降低)对Timothy S P和Hutchings I M的模型进行了修正,修正后的模型可以定量的描述绝热剪切带内微孔洞的演化直至破坏的全过程,模型的描述与微观分析获得的实验结果有较好的一致性.     

不同取样方向AZ31B镁合金应变率效应

采用分离式Hopkinson压杆获得了冲击压缩方向与热轧态A231B镁合金板材法向分别成90°、45°及0°的动态应力一应变曲线,利用光学显微镜及透射电子显微镜对微观组织演化过程进行了分析。结果表明：应变率约为1 200 s-1,压缩方向与板面法向成90°时,孪晶的面积分数随应变量的增大逐渐增加,孪生是主要变形机制,其曲线为凹型;压缩方向与板面法向成45°及0°时,其塑性变形以位错滑移为主,曲线形状分别为近似线型和凸型;应变率约为2 800 s-1,压缩方向与板面法向成90°时,孪晶面积分数迅速增加,大多数晶粒取向发生7改变,有利于滑移,其曲线由较低应变率的凹形变为凸型。     

热轧TB2钛合金织构多晶板动态压缩性能的各向异性

利用Instron 电子拉伸机和分离式霍普金生压杠(SHPB)实验装置, 研究了准静态和动态压缩条件下热轧TB2钛合金织构多晶板的力学性能。对TB2钛合金板材的轧向、横向以及轧制平面内与轧向成45°等3个方向进行了压缩实验, 得到了不同应变速率下的应力-应变曲线。结果表明：热轧TB2钛合金板材不同方向上的流变应力均随应变速率的增加而增加, 表现出明显的应变速率强化效应。准静态和动态力学性能均表现出各向异性, 且准静态和动态压缩行为规律不一致。考虑准静态和动态变形时可能的塑性变形机制, 基于微观晶体塑性变形理论, 定性讨论了热轧织构多晶TB2钛合金板屈服强度的各向异性     

镁合金表面电弧喷涂纯铝的界面特性研究

采用电弧喷涂技术对ZK60和AZ91两种镁合金表面喷铝,为了提高界面结合性能,对喷后样品进行了真空条件下450℃保温2h和250℃真空热压1h两种不同的后处理,结果表明:两种处理工艺都能一定程度的提高界面性能,但是前一处理工艺基体晶粒显著长大,后一处理工艺则对基体的影响较小,并且同时改善了涂层自身的性能.     

Plastic deformation mechanisms ofAZ31 magnesium alloy under high strain rate compression

The twinning and slip activities of AZ31 magnesium alloy sheet at a strain rate of 1 200 s^-1 were investigated. Dynamically mechanical properties of various oriented samples were measured using Split Hopkinson Pressure Bar（SHPB）. Optical microscope observations reveal that the dominant deformation mechanism is twinning for 90° oriented sample, and is slip for 45° and 0° oriented samples. TEM analysis for samples at a strain of 0.3% shows that the main deformation mechanisms for 90°, 45° and 0° oriented sample are {1012} 〈 1011 〉 and {1011} 〈 1012 〉 twinning, basal slip and non basal slip, respectively. The main features of the true stress--true strain curves can be explained based on deformation mechanism analysis.     

冲击加载条件下AZ31B镁合金变形孪晶的微观特征

采用分离式Hopkinson压杆(SHPB)对A231B热轧板材沿轧向进行冲击实验,加载应变率约为1200 s-1．利用金相显微镜和透射电子显微镜观察微观组织特征。结果表明：在应变量约为0.003的条件下,压缩孪生{10?1}/<10?2>与拉伸孪生{1?02}/< 1?01>均为孪生塑性变形机制,这与准静态加载下单一的拉伸孪生机制不同。孪晶内部的微观特征演化过程包括：1）平行排列基面层错的出现;2）与孪晶界成特定角度平行排列位错线的形成;3）位错胞的产生。     

应变率对Mg-Gd-Y合金断裂机制的影响

对Mg-Gd-Y合金分别使用准静态压缩试验机、分离式霍普金森压杆、平头弹丸侵彻加载,研究了该合金在1×10-3,1×103,1×104s-1时,应变率对其断裂机制的影响.研究结果表明,在应变率为1×10-3 s-1时,呈现出脆性解理断裂特征;当应变率增加为1×103 s-1时,动态压缩后断口除了解理片层外,还出现了热软化带,变形局域化是裂纹形核的通道,最终导致材料的失效.在应变率约为1×104 s-1时,稳定侵彻阶段,绝热剪切带是更高应变率下导致材料断裂的原因,特定位置的绝热剪切带为相变带,应变率的提高有利于形成相变带.应变率是通过影响Mg-Gd-Y合金的热软化效果而影响其断裂机制的.     

α相含量对新型亚稳β钛合金动态力学性能的影响

通过对2A2F(Ti-2Al-9.2Mo-2Fe-0.1B)钛合金在相变点以下进行固溶处理,使用扫描电镜和电子背散射衍射对处理后的显微组织与其在高应变率条件下的动态力学性能的关系进行了研究.结果表明,在650～790℃范围内,随着固溶温度的升高,实验合金组织中初生α相减少,动态流动应力降低,均匀塑性应变升高.经650℃...     

Ti-6Al-4V合金绝热剪切敏感性与临界破碎速度关系研究

利用应力塌陷发生的临界应变作为参量对比了Ti-6Al-4V合金的4种典型组织的绝热剪切敏感性,同时利用Taylor杆实验技术测定了其临界破碎速度,分析了钛合金绝热剪切敏感性与临界破碎速度关系.结果表明:不同组织的Ti-6Al-4V合金绝热剪切敏感性存在差异,实验涉及到的4种组织中双态组织最难于发生绝热剪切破坏;在Taylor杆高速冲击条件下,4种不同组织的Ti-6Al-4V合金均由于发生绝热剪切变形而导致破坏,并且临界破碎速度与应力塌陷临界应变成正比.