利用氨的配合作用,采用配位沉淀法及后续煅烧处理制备具有分级多孔结构的准一维NiO粉末。通过与球形NiO比较,对纤维状NiO催化乙醇氧化的电催化性能进行研究。结果表明,纤维状NiO具有更大的比表面积(140.153 m2/g)以及更低的电阻率(4.5×105Ω·m),从而在碱性介质中对乙醇氧化反应具有更优越的电催化活性。在0.6 V极化电位下,纤维状NiO在100~900 s的电流衰减仅为0.00003%,远低于球形NiO,显示其更好的稳定性。这种特殊的形貌和分级多孔结构使纤维状NiO作为直接乙醇燃料电池的阳极电催化剂具有很大的应用潜力。 相似文献
5.
Preparation of fibrous nickel oxide particles 总被引:7,自引:0,他引:7
1 INTRODUCTIONThenickeloxide (abbreviatedasNiOthereafter)isaversatilematerialwhichhasbeenfoundmanyap plicationsinindustrialfields .Itisusedasthekeymaterialinmanufactureofbatteryelectrode ,cata lyst,thermalsensitiveelement ,gassensitiveele ment,functionalceramics ,glass ,electroniccompo nentsandsoon[18] .At present,theapproachesavailableforultrafineNiOparticlesproductionincludecarbonylmethod ,laserchemicalmethod ,pyrolysisbymicrowave ,sol gelmethod ,pyrolysisbyultrason ic ,precipitation … 相似文献
6.
以NiCl2·6H2O, CoCl2·6H2O和草酸为原料, 利用氨水为配位剂和溶液pH调节剂, 通过配位共沉淀-热分解法制备了棒状多孔NiCo2O4粉末, 采用X射线衍射、扫描电镜、透射电镜以及比表面积仪对前驱体和NiCo2O4粉末的形貌和结构进行了表征, 考察了溶液pH对前驱体粉末形貌和分散性的影响; 采用循环伏安法和计时电流法研究了乙醇在棒状多孔NiCo2O4粉末修饰的玻碳电极上的电催化性能。结果表明: 前驱体的形貌与溶液的pH有关, 热分解得到的NiCo2O4粉末继承了前驱体形貌, 呈多孔棒状, 比表面积为89 m2/g, 平均孔径为12.56 nm。该粉末对乙醇具有良好的电催化活性, 氧化峰电流与乙醇浓度、扫速的平方根均呈直线关系, 表明棒状多孔NiCo2O4粉末对乙醇的催化反应机理为扩散控制。 相似文献
7.
Thermodynamic analysis on preparation of fibrous NiO precursor powders with oxalate precipitation process 总被引:1,自引:1,他引:0
According to the principles of simultaneous equilibrium and mass balance, a series of thermodynamic equilibrium equations of Ni( Ⅱ)-C2 O4^2--NH3-NH4^+-H2O system at ambient temperature are deduced theoretically and the logarithm concentration versus pH value(lg[Ni^2+ ]r-pH) diagrams at different solution compositions are drawn. The results show that when pH is above 8.0, nickel ions coordinate with ammonia, the precipitation proceeds slowly accompanying with the release of nickel ions from the multi-coordinated Ni(NH3)n^2+ (n= 1, 2,…, 6) and the morphology of NiO powder precursor is fibrous; when pH is below 8.0, nickel ion directly reacts with C2O4^2- and the morphology of NiO powder precursor is of cubic-shape. Some experiments were made to confirm the relation between the total concentration of nickel ion and pH. It is shown that the thermodynamic mathematical model is correct and the calculated values are basically accurate. 相似文献
9.
采用草酸盐沉淀-前驱体热分解法制备不同成分的Fe_xNi_(1-x)(0x1)合金粉。采用XRD和SEM分别测试前驱体和合金粉的物相结构与形貌。结果表明:随着Ni含量增大,前驱体物相由FeC_2O_4·2H_2O逐渐向NiC_2O_4·2H_2O转变,形貌由短棒状向立方体、多面体转变。Fe_xNi_(1-x)合金粉的几何外形与前驱体基本一致,但结构上呈多孔状,且粒径变小。Fe_xNi_(1-x)合金粉的物相结构随其成分变化,由富铁的bcc结构向富镍的fcc结构转变。测试不同成分Fe_xNi_(1-x)合金粉与石蜡复合物的电磁参数,并计算其吸波性能,Fe0.5Ni0.5具有最大的电磁损耗能力,厚3.0mm时在6.82GHz处具有最小反射损耗RL,为-52.58dB。Fe0.6Ni0.4具有最大有效频宽,厚1.5mm时反射损耗小于-10dB的有效频宽达4.02GHz。 相似文献
10.
Bi2Mn4O10具有高的理论比容量, 被认为是一种理想的锂离子电池负极材料。本研究以硝酸铋和乙酸锰为原料, 采用聚丙烯酰胺凝胶法制备Bi2Mn4O10负极材料, 考察了制备条件对Bi2Mn4O10负极材料的物相、形貌及电化学性能的影响。结果表明: 在丙烯酰胺含量与总金属离子摩尔比为8 : 1, 葡萄糖浓度为1.11 mol/L, 热处理温度为873 K的条件下, 可得类球型、分散性良好的纯相Bi2Mn4O10粉末。作为负极材料, Bi2Mn4O10粉末在0.2C (1C=800 mA/g)倍率下循环50圈后可保持496.8 mAh/g的比容量, 容量保持率为76.9%; 3C倍率下放电容量为232 mAh/g。 相似文献