焙烧及改性对沸石吸附甲醛性能的影响

通过研究几种不同的焙烧方式对沸石吸附甲醛的影响,得出经过不同焙烧改性的沸石对甲醛均具有一定的吸附量,其中经过NaOH改性后再于400℃焙烧的沸石吸附量比较理想,达到0．1656g／g．     

Effect of fly ash on drying shrinkage of thermal insulation mortar with glazed hollow beads

Drying shrinkage of thermal insulation mortar with glazed hollow beads was measured by a vertical length comparator, and the influences of fly ash with different contents (0, 18%, 36%, and 54% were used) on the long-term drying shrinkage were discussed. The mass loss was measured by the weighting method and the pore structure was characterized using three different methods, including the light microscopy, the mercury intrusion porosimetry (MIP), and the nitrogen adsorption/desorption (NAD) experiments, and the correlations among them were researched. The results show that drying shrinkage process of thermal insulation mortar includes three steps with increasing curing time: the acceleration period (before 7 d), the deceleration period (7-365 d), and the metastable period (after 365 d). Drying shrinkage in the first stage (7 d before) increases quickly owing to the fast water loss, and its development in the last two stages is attributed to the increment of the pore volume of mortar with the radius below 50 nm, especially the increment of the pore volume fraction of the pore radius within the size range between 7.3 nm and 12.3 nm. There is no change in the drying shrinkage development trend of mortar with fly ash addition, and three steps in the service life, but fly ash addition in the mortar restrains its value. There is a linear relationship between the drying shrinkage and fly ash content, which means that drying shrinkage reduces with fly ash addition.     

Al掺杂ZnO薄膜的制备及其电学性能研究

采用溶胶-凝胶法在玻璃基底上制备掺杂铝的氧化锌薄膜.研究了不同的铝掺杂浓度、薄膜厚度以及退火温度对电阻率的影响,结果表明掺杂铝摩尔分数为2%、退火温度在550℃时电阻率最低,电阻率随着薄膜厚度的增加而减小.通过XRD和SEM对薄膜的组织结构和形貌进行了表征,结果表明样品表面相对平整、致密,AZO薄膜保持着ZnO六角纤锌矿结构,说明了Al原子对Zn原子的有效替位.     

聚丙烯纤维增强玻化微珠保温砂浆的干缩开裂性能

测试了聚丙烯纤维增强玻化微珠保温砂浆的干缩,采用圆环加速开裂方法对其早期硬化开裂进行了试验,研究了聚丙烯纤维掺量和尺寸对其干缩开裂的影响,用质量损失率来表征其失水量,并通过氮吸附方法分析了孔结构.结果表明:聚丙烯纤维增强玻化微珠保温砂浆的干缩随龄期呈快速期(7d前)、慢速期(7~365d)、亚稳期(365d后)3个阶段,第1阶段的干缩主要由砂浆的快速失水引起,后2个阶段的干缩归结于砂浆中小于50.0nm的孔结构,且与7.3~12.3nm的孔径分布线性相关;聚丙烯纤维的掺加未改变玻化微珠保温砂浆干缩3阶段的发展趋势,但可抑制其发展速率,降低裂缝开裂权重值,而且聚丙烯纤维的阻裂作用与其掺量和尺寸线性相关.     

引气剂对玻化微珠保温砂浆长期干燥收缩的影响

应用立式比长仪测试了玻化微珠保温砂浆长期(2a)干燥收缩,研究了引气剂掺量(质量分数,下同)对保温砂浆干燥收缩的影响;用称重法测试了保温砂浆的质量损失,以反映其失水程度;采用氮吸附法测试了保温砂浆的孔结构,探讨了其干燥收缩、失水程度与孔结构之间的关系.结果表明,保温砂浆的干燥收缩随龄期增长呈快速期(7d前)-慢速期(7~365d)-亚稳定期(365d后)三阶段发展特征,引气剂的加入没有从根本上改变这种三阶段式的发展趋势,但显著抑制了后两个阶段的干燥收缩幅度;第一阶段干燥收缩的快速发展主要是由保温砂浆快速失水造成的,而第二、三阶段的干燥收缩主要归结于硬化浆体中小于50.0nm,尤其是7.3~12.3nm的孔体积分数明显增加;引气剂的作用与其掺量成正比,但掺量过大时因其不再增加引气作用而不能对保温砂浆的干燥收缩产生更大影响.     

含铝物质抑制碱-硅酸反应研究

研究几种含铝物质对碱—硅酸反应的抑制作用,结合XRD、SEM/EDS分析其抑制机理。结果显示,烧铝矾土、Al(OH)3对碱—硅酸具有良好的抑制作用,掺加30%烧铝矾土或20%Al(OH)3能使碱—硅酸膨胀反应膨胀率下降至1%。化学试剂Al(NO3)3、Al2(SO4)3不能有效地抑制碱—硅酸反应。     

天然及改性沸石对水中Cr6+的吸附研究

对Cr6 的吸附效果,盐酸改性沸石的比氢氧化钠改性沸石的好,HDTMA改性沸石的比六次甲基四胺改性沸石的好;在无机和有机改性沸石中,经过400℃煅烧的沸石对Cr6 的吸附性能较好。     

煅烧凹凸棒土对聚合物改性水泥砂浆性能的影响

采用300、500、700、850℃煅烧后的凹凸棒土替代部分水泥，研究了不同煅烧温度的凹凸棒土替代率对聚合物改性水泥砂浆性能的影响。结果表明，聚合物改性水泥砂浆的稠度随着凹凸棒土替代率的增加而下降，但是煅烧温度的升高有助于减小这种影响，凹凸棒土煅烧温度达到700℃及以上且替代率在15%以内时，对砂浆的抗折及抗压强度、拉伸粘结强度、抗吸水性改善效果较为明显；煅烧凹凸棒土能够提高砂浆的体积稳定性，但煅烧温度达到500℃时，继续升高温度对砂浆干缩率的改善效果有限。