Microstructure and mechanical behavior of laser aided additive manufactured low carbon interstitial Fe49.5Mn30Co10Cr10C0.5 multicomponent alloy

Laser aided additive manufacturing(LAAM)was used to fabricate bulk Fe49.5Mn30Co10Cr10C0.5 interstitial multicomponent alloy using pre-alloyed powder.The room temperature yield strength(σy),ultimate tensile strength(σUTS)and elongation(εUST)were 645 MPa,917 MPa and 27.0％respectively.The as-built sample consisted of equiaxed and dendritic cellular structures formed by elemental segregation.These cellular structures together with oxide particle inclusions were deemed to strengthen the material.The other contributing components include dislocation strengthening,friction stress and grain bound-ary strengthening.The high εUTS was attributed to dislocation motion and activation of both twinning and transformation-induced plasticity(TWIP and TRIP).Tensile tests performed at-40℃and-130℃demonstrated superior tensile strength of 1041 MPa and 1267 MPa respectively.However,almost no twinning was observed in the fractured sample tested at-40℃and-130℃.Instead,higher fraction of strain-induced hexagonal close-packed(HCP)ε phase transformation of 21.2％were observed for fractured sample tested at-40℃,compared with 6.3％in fractured room temperature sample.     

大型水电工程前期准备延期的影响类型分析

讨论了成本考虑不足与水电工程项目施工前准备阶段延期的负面影响,以及发展中国家不能及时有效地交付项目与稀有资源浪费间的冲突。建议项目员工、开发商、政府官员和国际金融机构重视延期成本,找到成本与效益的平衡点。     

Effect of the addition of rare earths on the activity of alumina supported copper cobaltite in CO oxidation,CH4 oxidationand NO decomposition

The effect of the addition of small amounts of rare earths(Ln=La, Ce, Nd and Gd) to alumina supported copper-cobalt spinel oxide on the catalysts efficiency in CO and CH4 oxidation and in NO decomposition was investigated. Samples of Ln/Cu Co/Al catalyst were prepared and characterized by X-ray diffraction(XRD), X-ray photoelectron spectroscopy(XPS), atomic absorption spectroscopy(AAS), scanning electron microscopy-energy dispersive spectroscopy(SEM-EDS), H2-temperature-programmed reduction(H2-TPR), electron paramagnetic resonance(EPR) spectroscopy and low temperature nitrogen adsorption. The results showed that the addition of rare earths changed the surface state of the alumina supported copper-cobalt spinel catalyst. As a result, partial reduction of copper species was observed as well as migration of these species between the surface and the bulk. The Ln/Cu Co/Al catalysts behaved differently in oxidation and reduction processes. In oxidation processes where oxide structure was important, Ce/Cu Co/Al and Nd/Cu Co/Al were the most active catalysts. The catalyst Ce/Cu Co/Al was the most active in the oxidation reactions because of the availability and favorable surface distribution of the redox couples Cu+/Cu2+ and Ce3+/Ce4+. In NO decompostion, Ln-modified catalysts significantly improved the selectivity of the process to N2.     

铁素体渗氮工艺模拟

纯铁的莱勒图被广泛用于选择合金钢的渗氮工艺。本文首次采用计算热力学来确定AISI 4140钢的莱勒图。研究表明，AISI 4140钢的莱勒图与纯铁的存在明显差异。对AISI 4140钢进行了渗氮试验，目的是验证计算热力学的预测结果。扫描电镜结果显示化合物层中存在两种相，利用透射电镜对化合物层与扩散层界面的研究结果证实了γ′-Fe4N和ε-Fe2－3（C，N）相的共存。这些试验结果与用计算热力学建立的AISI 4140钢莱勒图高度吻合。     

一种用于故障隔离的参数区间包络线计算方法

基于参数区间的故障隔离方法的核心工具是区间判断阈值曲线,其计算一直是制约该方法发展的问题。参数区间动态轨迹包络线作为区间判断阈值曲线具有能够适用于多重参数故障隔离等优点,但包络线计算中的包裹效应问题在该领域内一直未能得到很好解决。介绍一种基于上、下函数的包络线计算方法,有别于区间算法计算的包络线随着迭代的进行而迅速变得肥大的可能性,采用该方法的仿真实验表明其计算的包络线的包裹效应得到很大程度上的减轻,可有效用于故障隔离的区间判断。     

以金属氧化物为原料改进燃烧法合成γ-LiAlO_2（英文）

提出一种合成γ-LiAlO_2的替代解决方案—改进燃烧法直接合成γ-LiAlO_2,并将其用于相对简单的反应体系中,原料为非氧化性化合物如Al_2O_3和LiOH,燃料为尿素。采用1:1、1.5:1和2:1的非化学计量Li/Al摩尔比,在900和1000°C下反应5 min,制备LiAlO_2,并对其组织和结构进行表征。考察Li/Al摩尔比对材料形貌和高γ射线辐照下材料稳定性的影响。结果表明,所得粉体的晶体结构为?-LiAlO_2和?-LiAlO_2,其取决于Li/Al摩尔比。因此,用该方法可以成功合成微砖状、多面体状和层状?-LiAlO_2,而无需任何后续处理。γ辐照结果表明,所得到的?-LiAlO_2不分解,只形成少量的Li_2CO_3;由此可以确定,辐照会导致固结,不利于氚的有效提取;结果证明,用燃烧法生产高纯度?-LiAlO_2不需要硝酸盐前驱体。     

重振美国水电行业面临的挑战

对目前美国水电行业现状、近期计划开发项目以及相关机构立法情况进行了简述。指出重振美国水电行业面临的国有水利基建融资困难和项目审批程序冗长等问题,建议美国总统特朗普能与相关政府机构合作重振美国水电行业。     

生物基油对白炭黑填充天然橡胶胶料加工性能和硫化特性的影响

通常使用的石油基加工油,比如重质环烷油(HNO)和轻质环烷油(LNO)具有潜在的致癌性。本文研究了一种新型生物基油——茶籽油(TO)可能会成为通用加工油的替代品。在进行试验对比时,还选择了另外两种生物基油,分别是棕榈油(PO)和椰子油(CO)。试验结果表明,所有研究的生物基油的热稳定性均高于轻质环烷油(LNO),在白炭黑填充天然橡胶(NR)配方中,配合生物基油的混炼胶加工性能比添加石油基油的胶料更加优异。主要表现为:生物基油的热稳定性高,在相同混炼条件下,与添加石油基油的混炼胶相比,添加生物基油能够提高白炭黑与天然橡胶的混合效率,改善白炭黑在天然橡胶基质中的分散性,提高混炼胶的塑化效果。加工油的不同类型和用量对混炼胶的硫化特性影响很小。通过试验结果分析,所研究的TO、PO和CO生物基油很有可能成为石油基加工油的替代产品。     

水射流钻进及其在采矿和爆破中的应用

高速水射流高速水射流系统主要由一台高压泵、一台增压器和一个适宜的喷嘴构成。使用的压力分三级:即低压(<100兆帕)、中压(100～240兆帕)和高压(>240兆帕)。喷嘴直径为0.1～1毫米,流量4～30升/分。在一旋转钻进头上每一喷嘴可能有一个、两个或三个喷口,而整个钻进系统可能包含10以上的喷嘴。     

液压支架液压系统的改进

液压支架的工作情况首先取决于它与围岩、工作面支护速度的相互关系,其特征主要是由液压设备保证的工作阻力、初撑力、移动力和移动速度。 研究确定,支架在难冒落顶板煤层中工作时,必须拥有150千牛/米~2的工作阻力。靠相应地提高泵站压力来提高初撑力在技术上有困难,而增加液压支柱的直径和数量又受到支架重量和外形尺寸的限制。现有的手动控制和远距离控制的增压器(压力转换器)增压比低,能力有限。自动控制连续动作的增压器仅仅应用在固定的装置上,因为重量和外形尺寸都大。目前液压系统的控制方法仅仅依靠所采用的压力表。