Re-examination of phase relations between solid solutions in R4Al2O9-R4Si2N2O7-R4Si2O10 (R=Y,Gd, Yb) systems

Samples in Si–Al-R-O-N (R = Y, Gd, Yb) systems were prepared by solid-state reactions using R₂O₃, Al₂O₃, SiO₂ and Si₃N₄ powders as starting materials. X-ray diffraction was done to investigate RAM-J(R) solid solutions [RAM = R₄Al₂O₉, J(R) = R₄Si₂N₂O₇] formation and their equilibrium with RSO (R₄Si₂O₁₀). Phase relations between RAM, J(R) and RSO at 1700 °C were summarized in a phase diagram. It was determined that a limited solid solution of RAM and RSO could be formed along RAM-RSO tie-line, while RAM and J(R) form a continuous solid solution along RAM-J(R) tie-line. In RAM-J(R)-RSO ternary systems, the RAM-J(R) tie-lines were extended towards the RSO corner to form a continuous solid solution area of JRAMss (R = Y, Gd, Yb). The established phase relations in the Si–Al-R-O-N (R = Y, Gd, Yb) systems may facilitate compositional selections for developing JRAMss as monolithic ceramics or for SiC/Si₃N₄ based composites using the solid-solutions as a second refractory phase.     

Dual effect synergistically triggered Ce:(Y,Tb)3(Al,Mn)5O12 transparent ceramics enabling a high color-rendering index and excellent thermal stability for white LEDs

Ce:Y₃Al₅O₁₂ transparent ceramics (TCs) with appropriate emission light proportion and high thermal stability are significant to construct white light emitting diode devices with excellent chromaticity parameters. In this work, strategies of controlling crystal-field splitting around Ce³⁺ ion and doping orange-red emitting ion, were adopted to fabricate Ce:(Y,Tb)₃(Al,Mn)₅O₁₂ TCs via vacuum sintering technique. Notably, 85.4 % of the room-temperature luminescence intensity of the TC was retained at 150 °C, and the color rendering index was as high as 79.8. Furthermore, a 12 nm red shift and a 16.2 % increase of full width at half maximum were achieved owing to the synergistic effects of Tb³⁺ and Mn²⁺ ions. By combining TCs with a 460 nm blue chip, a warm white light with a low correlated color temperature of 4155 K was acquired. Meanwhile, the action mechanism of Tb³⁺ ion and the energy transfer between Ce³⁺ and Mn²⁺ ions were verified in prepared TCs.     

Synthesis of nanopowders with low agglomeration by elaborating Φ values for producing Gd2O3-MgO nanocomposites with extremely fine grain sizes and high mid-infrared transparency

Refining ceramic microstructures to the nanometric range to minimize light scattering provides an interesting methodology for developing novel optical ceramic materials. In this work, we reported the fabrication and properties of a new nanocomposite optical ceramic of Gd₂O₃-MgO. The citric acid sol-gel combustion method was adopted to fabricate Gd₂O₃-MgO nanocomposites with fine-grain sizes, dense microstructures and homogeneous phase domains. Nanopowders with low agglomeration and improved sinterability can be obtained by elaborating Φ values. Further refining of the microstructure of the nanocomposites was achieved by elaborating the hot-pressing conditions. The sample sintered at 65 MPa and 1300 °C showed a quite high hardness value of 14.3 ± 0.2 GPa, a high transmittance of 80.3 %–84.7 % over the 3?6 μm wavelength range, due mainly to its extremely fine-grain size of Gd₂O₃ and MgO (93 and 78 nm, respectively) and high density.     

Biodegradable Polymeric Nanoparticles Containing an Immune Checkpoint Inhibitor (aPDL1) to Locally Induce Immune Responses in the Central Nervous System

Immunotherapy is an efficient approach to clinical oncology. However, the immune privilege of the central nervous system (CNS) limits the application of immunotherapeutic strategies for brain cancers, especially glioblastoma (GBM). Tumor resistance to immune checkpoint inhibitors is a further challenge in immunotherapies. To overcome the immunological tolerance of brain tumors, a novel multifunctional nanoparticle (NP) for highly efficient synergetic immunotherapy is reported. The NP contains an anti-PDL1 antibody (aPDL1), upconverting NPs, and the photosensitizer 5-ALA; the surface of the NP is conjugated with the B1R kinin ligand to facilitate transport across the blood-tumor-barrier. Upon irradiation with a 980 nm laser, 5-ALA is transformed into protoporphyrin IX, generating reactive oxygen species. Photodynamic therapy (PDT) further promotes intratumoral infiltration of cytotoxic T lymphocytes and sensitizes tumors to PDL1 blockade therapy. It is demonstrated that combining PDT and aPDL1 can effectively suppress GBM growth in mouse models. The proposed NPs provide a novel and effective strategy for boosting anti-GBM photoimmunotherapy.     

Achieving fabrication of highly transparent Y2O3 ceramics via air pre-sintering by deionization treatment of suspension

An easy albeit quite effective deionization suspension treatment was adopted to alleviate the detrimental effects related to the hydrolysis of Y₂O₃ in an aqueous medium. Fabrication of highly transparent Y₂O₃ ceramics with a fine grain size via air pre-sintering and post–hot isostatic pressing (HIP) treatment without using any sintering additive was achieved using the treated suspensions. The hydrolysis issue of Y₂O₃ powder in an aqueous medium was effectively alleviated by using deionization treatment, and a well-dispersed suspension with a low concentration of dissolved Y³⁺ species was obtained. The dispersed suspensions were consolidated by the centrifugal casting method, and the green bodies derived from the suspension of 35.0 vol% solid loading showed an improved homogeneity with a relative density of 52.1%. Fully dense Y₂O₃ transparent ceramic with high transparency was obtained by pre-sintering consolidated green compacts at a low temperature of 1400°C for 16 h in air followed by a post-HIP treatment at 1550°C for 2 h under 200 MPa pressure. The sample had a fine average grain size of 690 nm. The in-line transmittance of the sample reached 83.3% and 81.8% at 1100 nm and 800 nm, respectively, very close to the theoretical values of Y₂O₃.     

Highly oriented α-Al2O3 transparent ceramics shaped by shear force

Alumina platelets were arranged horizontally in submicron alumina particles by shear force in the flow of slurries during casting. The obtained alumina green bodies with platelets were pressureless-sintered in vacuum, producing ceramics with thoroughly oriented grains and high transmittance. The effects of sintering parameters on the densification, microstructure evolution, and orientation degree of alumina ceramics were investigated and discussed. The results showed that the densification, grain size, orientation degree, and in-line transmittance were increased with increasing sintering temperature. The enhancement of orientation degree was mainly coherent with grain growth. The grain-oriented samples exhibited a much higher in-line transmittance (at 600 nm) of 61 % than that of the grain random sample (29 %). Moreover, the transmission remained a high level in the ultraviolet range (<300 nm).     

Toughness and R-curve behaviour of laminated Si3N4/SiCw ceramics

Laminated Si₃N₄/SiC_w ceramics were successfully prepared by tape casting and hot-pressing. Its mechanical properties were measured and the impact resistance was discussed. The toughness of the laminated Si₃N₄/SiC_w ceramics was 13.5 MPa m^1/2, which was almost 1.6 times that of Si₃N₄/SiC_w composite ceramics, namely 8.5 MPa m^1/2. Moreover, the indentation strength of laminated Si₃N₄/SiC_w ceramics was not sensitive to increasing indentation loads and exhibited a rising R-curve behaviour, indicating that the laminated Si₃N₄/SiC_w ceramics had excellent impact resistance. The improved toughness and impact resistance of laminated Si₃N₄/SiC_w ceramics was attributed to the residual stress caused by a thermal expansion coefficient mismatch between the different layers, resulting in crack deflection and bridging of SiC whiskers in the interface layer, thus consuming a large amount of fracture work.     

Electrodeposition of B,Ni co-doped diamond-like carbon films on AZ91D magnesium alloy: Corrosion and wear resistance

Diamond-like carbon (DLC) possesses brilliant and excellent properties, including excellent corrosion resistance as well as outstanding wear resistance. Ni and B co-doped DLC films were deposited on AZ91D magnesium alloy by electrodeposition under mild conditions (300 V and 25°C). Uniform and dense morphology of co-doped DLC films were observed, and Ni and B were uniformly incorporated into the carbon-based films. Among all the electrodeposits, the appearance of D and G peaks near 1330 and 1570 cm⁻¹ revealed that the as-deposited films were typical DLC films. As the addition of Ni was increased to 0.05 g, the highest microindentation hardness, the lowest friction coefficient, and wear loss were achieved to be 164.5 HV, 0.3, and 0.6 × 10⁻⁵ kg/m, respectively. The amorphous carbon films fabricated at 0.05 g Ni had the lowest corrosion current density and the most positive corrosion potential, which was mainly due to the small and dense granular structure effectively hindering the penetration of corrosion media.     

Performance of Al2O3 particle reinforced glass-based seals in planar solid oxide fuel cells

Glass-based materials are usually considered as excellent seals for jointing adjacent components in planar solid oxide fuel cells, but the uncontrollable crystallization in the glass may cause delamination and micro-cracks in such seals. To solve this problem, Al2O3 ceramic particles were added to a BaO–CaO–Al2O3–B2O3–SiO2 glass system to reduce negative effects caused by crystalline phase on the gas tightness and the joint strength in the seals. At an operating temperature of 750 °C, the glass-based seals with 20 wt% Al2O3 addition (GA80) exhibited extremely low leakage rates (~0.002 sccm/cm under an input gas pressure of 13.6 kPa) and higher shear strength (3.31 MPa). The Al2O3 ceramic addition and the crystalline phase BaAl2Si2O8 reinforced the glass matrix. Further thermal cycle analyses indicated that leakage rates for the GA80 seals remained at around 0.0025 sccm/cm after 10 thermal cycles, which was consistent with minor microstructural change and good interface bonding. Single cell testing with of GA80 seals was performed and the results demonstrated stable electrochemical performance through 6 thermal cycles at an open circuit voltage of 1.16–1.18 V, as well as a power density above 546 mW/cm2 at a current density of 925 mA/cm2. These results showed the high thermal cycle stability of the glass/Al2O3 composite seals in intermediate temperature planar solid oxide fuel cells.     

Phase and microstructure evolution of Sc2O3–CeO2 –ZrO2ceramics in Na2SO4 + V2O5 molten salts

In this study, the destabilization resistance of Sc₂O₃ and CeO₂ co-stabilized ZrO₂ (SCZ) ceramics was tested in Na₂SO₄ + V₂O₅ molten salts at 750°C–1100 °C. The phase structure and microstructure evolution of the samples during the hot corrosion testing were analyzed with X-ray diffraction (XRD), Raman spectra, scanning electron microscopy (SEM), energy dispersive X-ray spectrum (EDS), and X-ray photoelectron spectroscopy (XPS). Results showed that the destabilization of SCZ ceramics at 750 °C was the result of the chemical reaction with V₂O₅ to produce m-ZrO₂ and CeVO₄, and little ScVO₄ was detected in the Sc₂O₃-rich SCZ ceramics. The primary corrosion products at 900 °C and 1100 °C were CeO₂ and m-ZrO₂ due to the mineralization effect. The Sc₂O₃-rich SCZ ceramics exhibited excellent degradation resistance and phase stability owing to the enhanced bond strength and the decreased size misfit between Zr⁴⁺ and Sc³⁺. The destabilization mechanism of SCZ ceramic under hot corrosion was also discussed.