浅谈外墙干粘石

研究探索外墙干粘石装饰材料,通过工程实践予以改进。     

Numerical studies on the stress distribution in weldbonded joints with different adhesives

The Effect of elastic modulus and thickness of the adhesives on the stress distribution in weldbonded joints hasbeen studied with three-dimensional elastoplastic finite element method (FEM). Stress distribution curves have beenobtained at the edges of the spot welds and the lap zones in weldbonded joints, which werem made with adhesives ofdifferent elastic modulus or different thickness. Results show that there exists larger stress concentration at the edge of thespot Welds, though the shear stresses in the adhesive layers are smaller for weldbonded joints with low elastic modulus orthick adhesive layers. the stress concentration decreases and the shear stresses in adhesive layers increase with the increaseof the elastic modulus or the decrease of the adhesive thickness. It is concluded that the thiner adhesive layers with higherelastic modulius are preferable in weldbonded joints to cut down the stress concentration.     

工程机械用800 MPa低合金高强度钢焊接接头低周疲劳性能研究

针对大型工程机械用800 MPa低合金高强度钢及其焊接接头,进行低周疲劳性能研究。试验在常温下进行,对称三角波加载。试验结果表明,母材两个轧制方向的应变疲劳寿命没有明显差别,焊接接头的疲劳寿命偏低。焊接接头的局部软化是应变集中,导致应变疲劳寿命降低的主要原因。应变疲劳断口有明显的条纹特征,母材疲劳断口上伴有与条纹平行的二次裂纹,焊接接头的疲劳断口条纹清晰且宽度较细。试验确定的循环应力应变特性参数和应变疲劳寿命参数有明显的相关关系。     

坦克扭力轴的预扭处理及极限承载的数值模拟

为评定某坦克扭力轴的现预扭处理工艺,用弹塑性有限元分析方法,模拟了扭力轴的预扭过程及极限加载过程．给出了预扭至最大角度、预扭释放后自由态、工作扭转至最大角度3种状态下轴体内的应力分布．结果表明,预扭后扭力轴弹性工作应力范围得到极大扩展,其主要原因在于预扭塑变形成的表面残余应力．扭力轴目前所采用的预扭强化工艺远没有发挥出材料的最大潜能．     

稀土Ce加速Sn晶须生长的研究

稀土被认为是金属中的"维他命",在钎料中添加微量的稀土Ce可以显著地改善钎料合金的综合性能.然而,当钎料中添加过量的稀土时,将会发现Sn晶须的快速生长现象.结果表明,如果将Sn3.8Ag0.7Cu1.0Ce钎料内部的稀土相暴露于空气中,稀土相将发生氧化而产生体积膨胀,钎料基体对体积膨胀的抑制作用将使稀土相内部产生巨大的压应力从而加速Sn晶须的生长.     

Synthetically quantitative evaluation function of characteristic parameters on CO_2 arc welding process

0　ＩｎｔｒｏｄｕｃｔｉｏｎＣＯ2 ｓｈｉｅｌｄｅｄａｒｃｗｅｌｄｉｎｇｉｓｏｎｅｏｆｅｃｏｎｏｍｉｃａｌｗｅｌｄｉｎｇｔｅｃｈｎｏｌｏｇｙｗｉｔｈｈｉｇｈｅｒｅｆｆｉｃｉｅｎｃｙ ,ｌｏｗｅｒｅｎｅｒｇｙｃｏｎｓｕｍｐｔｉｏｎａｎｄａｎｔｉ ｏｘｉｄａｔｉｏｎ ,ｂｕｔｉｔｈａｓｔｈｅｓｈｏｒｔａｇｅｓｏｆｔｏｏｍｕｃｈｓｐａｔｔｅｒｉｎｇａｎｄｕｎｓａｔｉｓｆｙｉｎｇｗｅｌｄｉｎｇｆｏｒｍａｔｉｏｎｔｈａｔｒｅｓｔｒａｉｎｉｔｓｆｕｒｔｈｅｒｐｏｐｕｌａｒｉｚａｔｉｏｎａｎｄａｐｐｌｉｃａｔｉｏｎ .…     

AZ91铸造镁合金缺陷的超声检测技术

以AZ91铸造镁合金试块上的人工孔形缺陷为检测对象,研究缺陷的直径及埋藏深度与超声A扫描信号特征量的关系。结果表明,缺陷信号幅值与孔形缺陷直径及其埋藏深度有良好的线性关系。采用低通滤波和小波分析的方法对从镁合金试块上采集到的弱信号进行降噪处理,结果表明,小波变换能有效提高小孔径缺陷信号的信噪比。     

稀土Y加速Sn晶须生长规律

氧原子向稀土相YSn3晶格内部的扩散使YSn3产生体积膨胀,而周围钎料基体对体积膨胀的抑制作用使其内部产生巨大的压应力,此压应力为Sn晶须的生长提供了驱动力;与此同时,稀土相YSn3氧化过程中释放出的自由Sn原子为Sn晶须的生长提供了生长源.对空气中室温与150℃时效条件下稀土相YSn3表面Sn晶须的生长进行了研究.结果表明,室温时效条件下,稀土相YSn3表面Sn晶须的生长速度缓慢且分布不均;高温时效条件下,稀土相YSn3表面Sn晶须的生长速度较快且巨大的压应力使钎料基体发生了隆起现象.     

Sn晶须形态的研究

添加微量稀土可以有效地改善钎料的综合性能.然而当钎料中添加过量的稀土时,钎料内部会形成体积较大的稀土相.如果将稀土相暴露于空气中,其将发生氧化,氧化产生的压应力将加速稀土相表面Sn晶须的生长.研究了CeSn3与YSn3与ErSr3稀土相表面Sn晶须的生长情况.研究结果表明,稀土相表面出现了Sn晶须的快速生长现象,且试验中发现了一些特殊形态的Sn晶须.     

SnAgCuY钎料表面Sn晶须的旋转生长现象

研究了Sn3.8Ag0.7Cu1.0Y钎料表层上YSn3稀土相表面Sn晶须的生长行为。结果表明:室温时效条件下在YSn3的表面会出现Sn晶须的快速生长现象,生长速度最快可达10–10m/s,长度最长可达200μm。YSn3稀土相氧化的不均匀性是导致Sn晶须在生长时产生各种旋转现象的主要原因。