Effective parameters on diameter of carbon nanotubes by plasma enhanced chemical vapor deposition

The effective parameters on the diameter of carbon nanotubes (CNTs) by plasma enhanced chemical vapor deposition (PECVD) were presented.Among lots of influential parameters,the effects of the catalytic film thickness and the pretreatment plasma power on the growth of CNTs were investigated.The results show that the size of catalytic islands increases by increasing the thickness of catalytic layer,but the density of CNTs decreases.The pretreatment duration time of 30 s is the optimal condition for growing CNTs with about 50 nm in diameter.By increasing the pretreatment plasma power,the diameter of CNTs decreases gradually.However,the diameter of CNTs does not change drastically from 80 to 120 W.The uniformly grown CNTs with the diameter of 50 nm are obtained at the pretreatment plasma power of 100 W.     

Optical diffraction gratings embedded in BK-7 glass by low-density plasma formation using femtosecond laser

The optical embedded diffraction gratings with the internal refractive index modification in BK-7 glass plates were demonstrated using low-density plasma formation excited by a high-intensity femtosecond (130 fs) Ti: sapphire laser (λp=790 nm). The refractive index modifications with diameters ranging from 400 nm to 4 μm were photoinduced after plasma formation occurred upon irradiation with peak intensities of more than 1×1013 W/cm2. The graded refractive index profile was fabricated to be a symmetric around the center of the point at which low-density plasma occurred. The maximum refractive index change (Δn) was estimated to be 1.5×10-2. Several optical embedded gratings in BK-7 glass plate were demonstrated with refractive index modification induced by the scanning of low-density plasma formation.     

~(27)Al MAS-NMR study of inorganic polymer formation at ambient temperature

Inorganic polymers are a novel class of materials formed by the polymerization of silicon, aluminium and oxygen species to form an amorphous three-dimensional framework structure. The basis of this process is the alkaline solutions to induce a certain amount of Si and Al atoms to dissolve from a feedstock such as aluminosilicate. A study of 27Al MAS-NMR was carried out in an attempt to understand the reaction mechanism of the inorganic polymerization at ambient temperature. Scanning electron microscopy (SEM) and X-ray diffractometry (XRD) were also employed to establish the composition and microstructure of the inorganic polymerization. Specimens were prepared with different Al/Si mole ratios from the starting materials. The higher the Al content, the more sufficient the Al atoms that can combine with SiO4, and the longer the reaction time, the more the bonded Si—O—Al—O polymer structure, and then the higher the Al content, the fewer the octahedral Al with a uniform Si—O—Al—O structure in four directions, because four Al atoms are combined with SiO4, resulting in a uniform Si—O—Al—O structure in four directions. The results show that they have an amorphous microstructure.     

Hybrid functional IrO_2-TiO_2 thin film resistor prepared by atomic layer deposition for thermal inkjet printheads

IrO2-TiO2 thin films were prepared by atomic layer deposition using Ir(EtCp)(COD) and titanium isopropoxide (TTIP). The resistivity of IrO2-TiO2 thin films can be easily controlled from 1 500 to 356.7 μΩ·cm by the IrO2 intermixing ratio from 0.55 to 0.78 in the IrO2-TiO2 thin films. The low temperature coefficient of resistance(TCR) values can be obtained by adopting IrO2-TiO2 composite thin films. Moreover, the change in the resistivity of IrO2-TiO2 thin films was below 10% even after O2 annealing process at 600 °C. The step stress test results show that IrO2-TiO2 films have better characteristics than conventional TaN0.8 heater resistor. Therefore, IrO2-TiO2 composite thin films can be used as a heater resistor material in thermal inkjet printhead.     

Fabrication of curved micro structures on photoresist layer

A novel fabrication process for micro patterns with curvature was introduced. The curved structures were made by compensating rectangular micro structures with liquid photoresist layer. Because of the surface tension of the liquid in micro scale, various shapes of meniscus can be made on the micro channels. The micro channels were made on the silicon substrate in advance, and then the liquid layer was coated on the micro channels. From the nature of liquid behavior, the curved patterns with smooth surface are obtained, which cannot be made easily with the conventional mechanical machining, as well as with the microfabrication processes, such as wet and dry etching. With this principle, it is expected that the smooth and curved surfaces can be made by simple processes and the results can be applied widely, such as optical patterns.     

Reliability of flip-chip bonded RFID die using anisotropic conductive paste hybrid material

A reliability of flip-chip bonded die as a function of anisotropic conductive paste (ACP) hybrid materials, bonding conditions, and antenna pattern materials was investigated during the assembly of radio frequency identification(RFID) inlay. The optimization condition for flip-chip bonding was determined from the behavior of bonding strength. Under the optimized condition, the shear strength for the antenna printed with paste-type Ag ink was larger than that for Cu antenna. Furthermore, an identification distance was varied from the antenna materials. Comparing with the Ag antenna pattern, the as-bonded die on Cu antenna showed a larger distance of identification. However, the long-term reliability of inlay using the Cu antenna was decreased significantly as a function of aging time at room temperature because of the bended shape of Cu antenna formed during the flip-chip bonding process.     

Effects of Cr interlayer on mechanical and tribological properties of Cr-Al-Si-N nanocomposite coating

Cr-Al-Si-N coatings were deposited on SUS 304 substrate by a hybrid coating system. A Cr interlayer was introduced between Cr-Al-Si-N coating and SUS 304 substrate to improve the coating adherence. The effects of Cr interlayer on the microhardness, adhesion, and tribological behavior of Cr-Al-Si-N coatings were systematically investigated. The results indicate that the microhardness of the Cr-Al-Si-N coatings gradually deceases with increasing thickness of Cr interlayers. The adhesion between Cr-Al-Si-N and SUS 304 substrate is improved by addition of the Cr interlayers. A peak critical load of ~50 N is observed for the coating containing Cr interlayer of 60 nm as compared ~ 20 N for the coating without Cr interlayer. The thicker Cr interlayers result in reduced critical load values. Moreover, the wear resistance of the Cr-Al-Si-N coatings is greatly enhanced by introducing the Cr interlayer with thickness of 60 nm in spite of the decreased microhardness. The friction coefficient of the coating system is also moderately reduced.     

中国高等教育大众化出现的问题及对策

随着高等教育大众化时代的到来,中国高等教育面临着学龄人口减少、教学质量下降、财政运行困难和毕业生就业难等问题。针对上述问题,提出了致力高等教育国际化、大力发展成人教育、加强校企合作、强化特色办学和严格执行教师资格认定制度等对策。     

Formation of interfacial brittle phases sigma phase and IMC in hybrid titanium-to-stainless steel joint

The microstructures of the brazed joints for commercially pure Ti and stainless steel were investigated by the applications of various filler alloys including Ag-, Ti-, Zr- and Ni-based alloys. Generally, the dissimilar joints between Ti and stainless steel were dominated by the Ti-based intermetallic compounds (IMCs), e.g. (Ti, Zr)2(Fe, Ni), TiFe, TiCu, and Ti2(Fe, Ni), due to a significant dissolution of Ti from the base metal. The (Fe-Cr) σ phase was also observed near the stainless steel due to a segregation of Cr into the interface region. This research demonstrates empirically that the brittleness of the Ti and stainless steel joint can not be avoided only by applying single braze alloy or single insert metal, and thus an introduction of additional suitable interlayer between the filler alloy and the base metal is necessary to prevent the brittleness of the joint.     

Collapse behavior evaluation of hybrid thin-walled member by stacking condition

The recent trend of vehicle design aims at crash safety and environmentally-friendly aspect. For the crash safety aspect, the energy absorbing members should absorb collision energy sufficiently but for the environmentally-friendly aspect, the vehicle structure must be light weight in order to improve the fuel efficiency and reduce the tail gas emission. Therefore, the light weight of vehicle must be achieved in a securing safety status of crash. An aluminum or carbon fiber reinforced plastics (CFRP) is rep...