钕镱共掺钇铝石榴石纳米粉体

采用溶胶-凝胶燃烧法,制备了钕镱共掺钇铝石榴石(Nd3+/Yb3+:YAG)透明陶瓷纳米粉体,并用热分析、X射线衍射、红外光谱、透射电镜、吸收及荧光光谱等测试方法对其结构、形貌及性能进行分析.结果表明:经900℃煅烧,Nd3+/YB3+:YAG透明陶瓷的质量损失为49.56%,所得到的Nd3+:Yb3+:YAG纳米粉体结晶好,烧结性好,纯度较高,形状规则,粒径均匀,均在60～100衄之间.在808 nm处具有较强的吸收带,对应于Nd离子4I9/2-4F7/2跃迁,有利于对808nm激光二级管泵浦光的吸收.在1064nm处,Nd3+/Yb3+:YAG的发射峰要强于Nd3+:YAG,说明在Nd3+/Yb3+:YAG中,通过[(4F3/2)Nd),(2F7/2)Yb]→[(4I9/2)nd,(2F5/2)Yb]离子问的交叉弛豫,产生了有效的Yb3+到Nd3+的能量转移,从而实现激光的高效输出.     

铽镓石榴石陶瓷制备及热光性能

铽镓石榴石(Tb_3Ga_5O_(12),TGG)陶瓷具有大的Verdet常数和高的热导率等磁光性能。利用溶胶-凝胶法合成了TGG多晶料,采用真空烧结法制备出优质的TGG磁光陶瓷。采用X射线衍射、扫描电子显微镜和分光光度计等测试技术,对合成的TGG多晶料和陶瓷的性能进行了表征。结果表明:多晶料中的晶粒粒径小、分布均匀,可用于TGG陶瓷的制备。TGG磁光陶瓷的Verdet常数分别与温度和波长的平方成反比。对热膨胀系数和热光系数等热光性能进行了分析,发现降低温度,可有效抑制TGG陶瓷元件的热光效应。因此,制备的TGG磁光陶瓷可用于替代TGG磁光晶体。     

浅析长江电力通信部门安全管理体系建设

通信设备设施多,且站点分散,安全技术管理需要有新的思考和探索。通过创新摸索,实施"通信小微"项目,将机房各种告警信息采集通过微信进行推送,实时掌握设备运行状况;"光缆三维建模"和"光缆在线监测"项目的实施,提供了电站光缆的布局情况和路由情况,光缆管理更加直观和方便。"安全工器具的二维码技术管理"项目,将二维码的共性与安全工器具的管理相结合,更加方便快捷管理。     

掺镱钇铝石榴石激光晶体生长与开裂

采用提拉法生长了掺杂5%(摩尔分数)Yb3+的Yb:Y3Al5O12(Yb:YAG)晶体,并对晶体生长工艺进行了研究。从理论上分析了生长速率、转速、热应力、晶体尺寸对晶体开裂的影响。确定的最佳工艺条件为:晶体放肩和等径生长速率分别为0.8mm/h和1mm/h;转速为15r/min;轴向温度梯度为0.01～0.05℃/mm。所得晶体的最佳直径为15～25mm。     

新型太阳能电池封装材料的研究进展

迅猛发展的太阳能电池封装材料,己成为全球光伏领域大力研究的热点之一。为了解太阳能电池封装材料的发展方向和研究进展,本文介绍了传统封装材料的基本要求和组成,针对传统封装材料的缺点,指出了封装材料的改进主要集中在对新型树脂替代EVA和玻璃的研究;综述了新型封装材料特别是聚氨酯材料、电气绝缘材料和背板材料的研究进展和发展方向。     

Spectral properties of Tm,Ho:LiYF4 laser crystal

The LiYF4 single crystal codoped with thulium and holmium ions was successfully grown by the Cz method. The optimal technical parameters obtained were as follows: the pulling rate was 0.16 mm/h; the rotation speed was 3 rpm; the cooling rate was 15 °C/h. The result of XRD curve showed that as-grown Tm,Ho:LiYF4 laser crystal belonged to the monoclinic system with scheelite-type structure and space group I41/a. The cell parameters calculated were: a=0.52160 nm, c=1.09841 nm and Z=4. Absorption and fluorescence spectra of Tm,Ho:LiYF4 laser crystal at room temperature were measured and analysed. The absorption cross section, FWHM and absorption coefficient at 779.3 nm calculated were 7.44×10-21 cm2, 8.7 nm and 2.23 cm-1, respectively. An intensive fluorescence emission peak appeared near 2045 nm. The emission cross section and fluorescence lifetime were 0.87×10-20 cm2 and 10.8 ms, respectively. The ratio of Tm-Ho transfer to its back-transfer process was 10.6.     

如何建立有线数字电视网安全播出系统体系的措施

有线电视网是一种全新的电视组织形态,它在我国的产生和发展,为我国媒体国际传播能力的增强奠定了坚实的基础,在一定程度上促进了我国主流媒体海外舆论阵地的建设。安全播出系统是有线数字电视网的核心技术平台,必须做到合理的规划和建设。文章分析了我国有线数字电视网播出系统的现状,并对建立有线电视网安全播出系统体系的措施做了探讨。     

笼型倍半硅氧烷环氧树脂的合成与表征

以3-缩水甘油丙氧基三甲氧基硅烷(GTMS)为原料在异丙醇(IPAP)中水解缩合制成笼型倍半硅氧烷环氧树脂(POSSEP),用红外光谱(FTIR)、~1H-NMR、热重分析(TGA)和液相色谱-质谱联用仪(LC/MS)对其结构进行了表征。LC/MS分析结果表明,合成的笼型倍半硅氧烷环氧树脂以T_(10)为主,另外还含有一定量的T_8以及少量的T_9。热重分析结果表明,笼型倍半硅环氧树脂具有良好的耐热性。在失重5%时的温度为364．5℃,在444．7℃时降解速率最快,800℃以后笼型硅环氧树脂质量基本不变,900℃时的剩余质量为40%。