Mechanical properties and thermal shock in thin ZrO2–Y2O3–Al2O3 films obtained by the sol-gel method

Thin multilayer coatings of ZrO₂–Y₂O₃–Al₂O₃ were prepared using the sol-gel method and dip-coating technique in order to advance in the study of what influence the incorporation of Al₂O₃ has on films of Y₂O₃-doped ZrO₂, investigating its role in the synthesis of the solutions and in the characteristics and properties of the coatings. After the characterization of the solutions used in the process, the microstructure of the films was studied and their mechanical behaviour and resistance to thermal shock were determined so as to optimize the characteristics and functionality of these coatings. With increased alumina content, 3YSZ-Al₂O₃ (20 mol%), the cubic phase of the zirconia disappeared completely at the sintering temperature used (700 °C), resulting in the tetragonal phase with Al in solution. There was also a decrease in the coatings' hardness and Young's modulus, and an increase in toughness and resistance to thermal shock. These results allow guidelines to be established for the design of multilayer structures that are, tougher, more resistant, and have improved surface properties.     

Comparative Genomics Reveals 13 Different Isoforms of Mytimycins (A-M) in Mytilus galloprovincialis

Mytimycins are cysteine-rich antimicrobial peptides that show antifungal properties. These peptides are part of the immune network that constitutes the defense system of the Mediterranean mussel (Mytilus galloprovincialis). The immune system of mussels has been increasingly studied in the last decade due to its great efficiency, since these molluscs, particularly resistant to adverse conditions and pathogens, are present all over the world, being considered as an invasive species. The recent sequencing of the mussel genome has greatly simplified the genetic study of some of its immune genes. In the present work, we describe a total of 106 different mytimycin variants in 16 individual mussel genomes. The 13 highly supported mytimycin clusters (A–M) identified with phylogenetic inference were found to be subject to the presence/absence variation, a widespread phenomenon in mussels. We also identified a block of conserved residues evolving under purifying selection, which may indicate the “functional core” of the mature peptide, and a conserved set of 10 invariable plus 6 accessory cysteines which constitute a plastic disulfide array. Finally, we extended the taxonomic range of distribution of mytimycins among Mytilida, identifying novel sequences in M. coruscus, M. californianus, P. viridis, L. fortunei, M. philippinarum, M. modiolus, and P. purpuratus.     

A novel ceramic matrix composite based on YNbO4–TiO2 for microwave applications

This work presents the dielectric properties of YNbO₄ (YNO)–TiO₂ composites in the microwave range. X-ray diffraction analysis demonstrates that the addition of TiO₂ to YNO results in the formation of a Y(Nb_0.5Ti_0.5)₂O₆ phase. In the microwave range, the values of permittivity and dielectric loss did not present major changes with the increment of TiO₂. Moreover, the addition of TiO₂ results in an improvement in the thermal stability of YNO, with YNO63 demonstrating a resonant frequency of ?8.96 ppm.°C^?1. We utilised numerical simulations to evaluate the behaviour of these materials as dielectric resonator antennae and it is found that they exhibit a reflection coefficient below ?10 dB at the resonant frequency, with a realised gain of 4.94 – 5.76 dBi, a bandwidth of 665–1050 MHz and a radiation efficiency above 84%. Our results indicate that YNO–TiO₂ composites are interesting candidates for microwave operating devices.     

Portrait of Cancer Stem Cells on Colorectal Cancer: Molecular Biomarkers,Signaling Pathways and miRNAome

Colorectal cancer (CRC) is a leading cause of cancer death worldwide, and about 20% is metastatic at diagnosis and untreatable. Increasing evidence suggests that the heterogeneous nature of CRC is related to colorectal cancer stem cells (CCSCs), a small cells population with stemness behaviors and responsible for tumor progression, recurrence, and therapy resistance. Growing knowledge of stem cells (SCs) biology has rapidly improved uncovering the molecular mechanisms and possible crosstalk/feedback loops between signaling pathways that directly influence intestinal homeostasis and tumorigenesis. The generation of CCSCs is probably connected to genetic changes in members of signaling pathways, which control self-renewal and pluripotency in SCs and then establish function and phenotype of CCSCs. Particularly, various deregulated CCSC-related miRNAs have been reported to modulate stemness features, controlling CCSCs functions such as regulation of cell cycle genes expression, epithelial-mesenchymal transition, metastasization, and drug-resistance mechanisms. Primarily, CCSC-related miRNAs work by regulating mainly signal pathways known to be involved in CCSCs biology. This review intends to summarize the epigenetic findings linked to miRNAome in the maintenance and regulation of CCSCs, including their relationships with different signaling pathways, which should help to identify specific diagnostic, prognostic, and predictive biomarkers for CRC, but also develop innovative CCSCs-targeted therapies.     

Corrosion behavior of T24, T92, VM12, and AISI 304 steels exposed to KCl–NaCl–K2SO4–Na2SO4 salt mixtures

The corrosion mechanisms of T24, T92, VM12, and AISI 304 steels are studied under the influence of NaCl–KCl, NaCl–Na₂SO₄, and KCl–K₂SO₄ salt mixtures in a dry air atmosphere at 650°C for 15 days. NaCl–KCl was the most aggressive deposit and AISI 304 stainless steel exhibited the highest corrosion resistance. There was no relation between the Cr content of the ferritic steels and their corrosion resistance in NaCl–KCl. In contrast, the resistance of high-Cr steels was better when exposed to NaCl–Na₂SO₄ and KCl–K₂SO₄. The high-Cr and the low-Cr steels were more susceptible to NaCl–Na₂SO₄ and to KCl–K₂SO₄, respectively.     

Femtosecond Ti: Sa ultra short-pulse laser irradiation effects on the properties and morphology of the zirconia surface after ageing

Femtosecond pulses from a Ti:Sapphire laser were used to irradiate specimens of yttria-stabilised (35% mol) tetragonal zirconia (Y-TZP) with the purpose of studying the effects of the irradiations on their surface properties and morphology after ageing. Zirconia disks were divided into eight groups (n = 32) according to their surface treatment and subsequent ageing: Control: no treatment; sandblasting: Al₂O₃ sandblasting 50 μm; and ultrashort laser pulses irradiation with 25 μJ pulses, considering two different scanning steps based on the width between two grooves. These groups were duplicated and submitted to ageing. The surfaces were analysed using scanning electron microscopy (SEM), and X-ray diffraction. A finite element analysis, a biaxial flexure test, as well as fractographic and Weibull analyses, were performed. The strengths of the disks were statistically different for the treatment factor, and the principal stresses seemed to be concentrated at the centre of the specimens, as predicted by the computer simulations. Ageing decreased the strengths for all groups and increased the Weibull modulus for the laser group with the 40 μm-width between two grooves. The sandblasting group presented the highest monoclinic phase peak. Although the most significant strength was found within the sandblasting group, the phase transformation was favourable to the laser groups. The Weibull modulus was higher for the laser group with the 60 μm-width between two grooves, confirming the highest homogeneity of its failure distribution. Regardless of the surface treatment, strength was decreased with ageing in all groups. The femtosecond Ti:Sa ultra-short pulse laser irradiation can be suggested as an alternative to the gold standard sandblasting in long-term Y-TZP zirconia rehabilitations, such as crowns and veneers.     

Effect of different acids during the synthesis of urea-formaldehyde adhesives and the mechanical properties of medium-density fiberboards bonded with them

The characteristics of urea-formaldehyde (UF) adhesives condensed by catalysis with four different acids, namely formic (HCOOH), hydrochloric (HCl), phosphoric (H₃PO₄), and sulfuric (H₂SO₄) acids, under alkaline–acidic–alkaline conditions at a molar ratio F/U = 1.12 were studied. The thermal curing properties of UF adhesives catalyzed with acid were characterized by differential scanning calorimetry at 10 °C/min heating rate. The resin structure examined by ¹³C-NMR spectroscopy showed that the resin catalyzed with HCl had a lower proportion of methylol groups, resulting in a lower level of formaldehyde emission. It was interesting to note that HCOOH resulted in the best overall mechanical properties of the medium-density fiberboard (MDF) panels. The HCl catalyst resulted in the poorest performance, providing the lowest internal bond strength, modulus of elasticity, and thickness swelling, with the exception of the free formaldehyde content. The resin catalyzed with H₂SO₄ had the highest free formaldehyde and the highest formaldehyde emission. H₂SO₄ and H₃PO₄ resulted in MDF mechanical properties relatively lower than for HCOOH. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019 , 136, 47256.     

Polyetherimide-LaNi5 composite films for hydrogen storage applications

This study investigates the preparation of polyetherimide (PEI) – LaNi₅ composites films for hydrogen storage. Prior to the polymer addition, LaNi₅ was ball-milled at different conditions (250, 350, and 450 RPM) and annealed at 500 °C for 1 h under vacuum. The composites were produced with BM-LaNi₅-350 (PEI/LaNi₅-350) and annealed BM-LaNi₅-350 (PEI/LaNi₅-350-TT). Membranes were successfully produced through solvent casting assisted by an ultrasonic bath. The particles dispersion and the film morphology did not change after hydrogenation cycles. In the H₂ sorption experiments at 43 °C and 20 bar, the films stored H₂ without incubation time; both samples reached a capacity of ~0.6 wt%. The H₂ sorption kinetics of PEI/LaNi₅-350 was comparable to that of BM-LaNi₅-350, whereas PEI/LaNi₅-350-TT presented significantly slower kinetics. LaNi₅ oxidation was hindered by PEI, showing that it can be explored to improve metal hydrides air resistance. The results demonstrated that PEI films filled with LaNi₅ are promising materials for hydrogen storage.