Highly active sites of low spin FeⅡN4species:The identification and the ORR performance

Over recent years,catalytic materials of Fe-N-C species have been recognized being active for oxygen reduction reaction(ORR).However,the identification of active site remains challenging as it generally involves a pyrolysis process and mixed components being obtained.Herein Fe₃C/C and Fe₂N/C samples were synthesized by temperature programmed reduction of Fe precursors in 15%CH₄/H₂and pure NH₃,respectively.By acid leaching of Fe₂N/C sample,only single sites of FeN₄species were presented,providing an ideal model for identification of catalytic functions of the single sites of FeN₄in ORR.A correlation was conducted between the concentration of Fe^ⅡN₄in low spin state by Mossbauer spectra and the kinetic current density at 0.8 V in alkaline media,and such a structure-performance correlation assures the catalytic roles of low spin Fe^ⅡN₄ species as highly active sites for the ORR.     

氧化薄膜对锆-4合金表面性能的影响

为了研究氧化薄膜对Zr-4合金表面性能的影响,对样品分别进行了350℃和400℃各10 min,15 min,20 min和25 min氧化.结果发现,不同条件下氧化生成的样品表面呈现不同的颜色.小角掠射X射线衍射分析(GAXRD)表明,生成的氧化物为非化学计量的六方相氧化锆.样品在0.5 mol/L的H2SO4溶液中进行电化学试验发现,氧化后样品的耐电化学腐蚀性能有所提高.而用纳米压痕仪试验的结果表明,氧化后样品有较高的纳米硬度和较低的弹性模量,意味着氧化后样品可能有更好的耐磨性.400℃氧化样品对合金性能的提高优于350℃氧化样品.     

电致孔经皮给药：表面活性剂对孔道存在时间和药物传输的影响

Electroporation creates aqueous pathways by short high-voltage pulses resulting in a transient perme- abilization of stratum corneum and an increase in the transdermal delivery rate.However the aqueous pathways will reseal after pulsing,which leads to the rapid drop of transdermal flux.In the present study,the surfactants were added to the donor solution to hinder the shrinkage and resealing of the electropore,and to prolong the lifetime of the aqueous pathways with the consideration that the surfactants could reduce the surface energy of the electropore. These effects of surfactants were demonstrated by the dynamic electrical resistance of the skin and the fluorescent imaging of the local transport regions.Piroxicam（PIX）was transported percutaneously in the presence of surfactants in vitro.Owing to the longer lifetime of aqueous pathways,together with the promotion of PIX availability at the barrier exterior and the improvement in the partition of PIX into the aqueous pathways,the presence of surfactants led to a remarkable increase in the transdermal delivery rate during electroporation and a significant growth of the accumulative transdermal amount of PIX.     

马铃薯淀粉渣的羧甲基化研究

研究了马铃薯淀粉渣与氯乙酸进行羧甲基化反应的一般规律，考察了反应温度、反应时间、原料配比等因素对产物取代度的影响，通过正交试验，找到了最佳反应条件，并对产物性能进行了测试。     

燃煤和大气污染

介绍了煤炭作为中国主要能源在开发利用过程中对大气污染的计数据，论述了燃煤的洁净技术和污染控制技术，提出今后发展的目标     

局域网交换机体系结构对网络性能的影响

随着网络技术的发展,局域网技术从网桥技术、主干路由技术向局域网交换技术快速发展,局域网数据交换技术也发生了巨大的变换,局域网交换机的交换体系结构对网络性能的影响越来越大。     

碳离子注入纯锆后在1 mol/L硫酸溶液中的腐蚀行为

为了研究碳离子注入对纯锆耐蚀性的影响,用MEVVA源对纯锆样品进行了1×1016ions/cm2至1×1017ions/cm2的碳离子注入,注入加速电压为40 kV.用X射线光电子能谱(XPS)和俄歇电子谱(AES)分析了注入样品表层元素的价态和深度分布.透射电镜(TEM)用来观察碳离子注入样品的微观结构;碳离子注入样品后相结构的变化用掠角X射线衍射(GAXRD)来检测.纯锆注入样品随后浸入1 mol/L的硫酸溶液中,测其极化曲线以评价其耐蚀性.发现碳离子注入极大地提高了纯锆基体的耐蚀行为,剂量越高,耐蚀性越好.最后,对碳离子注入导致纯锆基体腐蚀行为发生改变的机理进行了讨论.     

镧离子注入对纯锆抗高温氧化性能的影响

对纯锆表面注入了1×10~(16)ions/cm~2～1×10~(17)ions/cm~2的镧离子,并在500℃条件下进行了空气氧化增重研究。用XPS分析了注入的镧、锆的价态;用AES分析了镧锆氧三元素的深度分布;用0.3°小角X光掠射(GAXRD)分析了高温氧化时氧化锆的相转变。结果表明,纯锆表面注入La离子后,其抗高温氧化性能显著提高,且注入剂量越大效果越强,注入氧化膜以La_2O_3和ZrO_22种形式存在;由于La离子的注入,促使形成大量四方相氧化锆(t-ZrO_2),而且减少四方相氧化锆(t-ZrO_2)向单斜相氧化锆(m-ZrO_2)的转变,这是纯锆氧化速率降低的根本原因。     

铸造合金流动性高精度测试装置试验研究

设计了一种提高螺旋试样法测试铸造合金流动性准确性的新装置，在单片机的控制下，通过自动浇注系统，可在预定的浇注温度和相同的压力下实现合金液的自动浇注。与传统流动性测试装置的试验结果对比表明，该装置在流动性测试的准确度和可重复性上有很大的提高。借助该装置，研究了铝合金浇注温度对流动性的影响，并得出两者之间的对应关系，发现流动性随浇注温度的升高呈非线性增长，最大增幅达16．5ram／℃。     

变质工艺对ZL102铝硅合金表面张力的影响

利用回归正交设计法设计了变质处理影响ZL102铝硅合金表面张力的试验方案，利用自行研制的表面张力快速测定仪炉前测定ZL102铝硅合金液的表面张力，建立了变质工艺影响ZL102铝硅合金表面张力的数学模型。结果表明，变质剂加入量对ZL102铝硅合金表面张力影响显著，变质时间次之，变质温度的影响不明显，交互相和二次相的影响可以忽略。进一步试验表明，利用该数学模型求得的表面张力值与实际测量值偏差较小。