Melting process and melt structure of fly ash/magnesium slag blends for the production of inorganic fibers

Fiber production from inorganic industrial solid wastes is an effective waste management strategy. Because of cost considerations, most enterprises generally use local solid wastes as raw materials to produce fibers. In this study, we explored the feasibility of producing fibers using fly ash and magnesium slag. The results show that the melting temperature of the blends composed of fly ash, magnesium slag, and a small amount of calcined dolomite first decreased and then increased with an increase in acidity coefficient (M_k) from 1.0 to 2.4_. The samples could form a eutectic system in the M_k range of 1.4–1.8, and therefore have a relatively low melting temperature in this M_k range. Fly ash could react with magnesium slag and calcined dolomite to form akermanite, gehlenite-magnesium, and anorthite at temperatures close to the melting temperature; therefore, these crystalline phases were the main reaction products formed in the samples with M_k values lower than 1.80. Anorthite reacted further with some Na-containing and Si-containing spieces to produce labradorite. Thus, the content of anorthite and labradorite rapidly increased and they became the major crystal phases in the blend samples with M_k values greater than 1.80. MAS-NMR spectroscopic analysis revealed that the network structure of the melts depended on the ratio of bridging oxygen to non-bridging oxygen; a high ratio of bridging oxygen to non-bridging oxygen could lead to the formation of a dense network structure in the melt. The blends of fly ash and magnesium slag can be used to produce wool fibers and continuous fibers. In addition, the suitable temperature ranges for the production of both types of fibers were determined. The drawing temperature for continuous fiber production depended on the degree of polymerization and structure of the melt.     

平行坐标技术在干式变压器温度场可视化分析中的应用

本文中笔者将平行坐标技术应用于变压器温度场多维可视化分析,以矿用变压器为例,给出了其高、低压绕组纵向温度分布.     

Effects of upholstery materials on the burning behavior of real‐scale residential upholstered furniture mock‐ups

Fire spread and growth on real‐scale four cushion mock‐ups of residential upholstered furniture (RUF) were investigated with the goal of identifying whether changes in five classes of materials (barrier, flexible polyurethane foam, polyester fiber wrap, upholstery fabric, and sewing thread), referred to as factors, resulted in statistically significant changes in burning behavior. A fractional factorial experimental design plus practical considerations yielded a test matrix with 20 material combinations. Experiments were repeated a minimum of two times. Measurements included fire spread rates derived from video recordings and heat release rates (HRRs). A total of 13 experimental parameters (3 based on the videos and 10 on the HRR results), referred to as responses, characterized the measurements. Statistical analyses based on Main Effects Plots (main effects) and Block Plots (main effects and factor interactions) were used. The results showed that three of the factors resulted in statistically significant effects on varying numbers of the 13 responses. The Barrier and Fabric factors had the strongest main effects with roughly comparable magnitudes. Foam was statistically significant for fewer of the responses and its overall strength was weaker than for Barrier and Fabric. No statistically significant main effects were identified for Wrap or Thread. Multiple two‐term interactions between factors were identified as being statistically significant. The Barrier*Fabric interaction resulted in the highest number of and strongest statistically significant effects. The existence of two‐term interactions means that it will be necessary to consider their effects in approaches designed to predict the burning behavior of RUF.     

川中地区侏罗系沙溪庙组致密气处理和解释关键技术与应用

四川盆地蕴含丰富的致密砂岩气资源，近期利用高精度三维资料开展侏罗系沙溪庙组河道砂体勘探取得突出成效。沙溪庙组河道砂体具有横向变化快、储层非均质性强的特点，因此提高河道砂体的边界识别及其含气性预测精度是致密气地震勘探的关键。通过开展AVO特征低频保护的“六分法”（分类、分频、分时、分域、分步和分区）高保真叠前去噪、近地表Q补偿和OVT域叠前时间偏移等技术攻关，形成了一套针对川中地区侏罗系沙溪庙组致密气藏的“双高”（高保真、高分辨率）地震处理技术，并创新应用“双亮点”属性及多波、多分量砂体含气性地震预测等解释技术，提高了含气砂体预测精度。该技术系列在川中沙溪庙组致密气预测应用成果显著，地震数据频带得到了拓宽，低频信息更加丰富，资料信噪比明显提升，河道边界及其含气性预测的精度大幅提高，钻井成功率超过83%，应用成果有力地支撑了该地区沙溪庙组致密气的增储上产。     

基于LID理论的海绵市政道路设计应用研究

从LID理论出发,阐述了下沉式绿化带、透水铺装、生态树池的雨水渗透和雨水量调蓄作用,指出市政道路中下沉式绿化带、透水铺装、生态树池3种设施组合下的设计应结合场地条件计算雨水调蓄和渗透量,对径流总量控制规模和径流污染控制量进行校核,通过实例分析,为下沉式绿化带在市政道路设计中的应用提供理论基础.     

Strong tribocatalytic dye degradation by tungsten bronze Ba4Nd2Fe2Nb8O30

The triboelectric effect has recently demonstrated its great potential in environmental remediation and even new energy applications for triggering a number of catalytic reactions by utilizing trivial mechanical energy. In this study, Ba₄Nd₂Fe₂Nb₈O₃₀ (BNFN) submicron powders were used to degrade organic dyes via the tribocatalytic effect. Under the frictional excitation of three PTFE stirring rods in a 5 mg/L RhB dye solution, BNFN demonstrates a high tribocatalytic degradation efficiency of 97% in 2 h. Hydroxyl radicals (?OH) and superoxide radicals (?O₂－) were also detected during the catalysis process, which proves that triboelectric energy stimulates BNFN to generate electron-hole pairs. The tribocatalysis of tungsten bronze BNFN submicron powders provides a novel and efficient method for the degradation of wastewater dye by utilizing trivial mechanical energy.     

一种组态控件技术在电力监控系统中的运用

主要阐述QGraphicsProxyWidget类在电力监控软组态软件中的运用.将整个图形窗口作为电力监控组态软件的图元,可以丰富电力监控软件的图形库并且提升工程人员的施工效率.     

Environmental effects on the strength and impact damage resistance of alumina based oxide/oxide ceramic matrix composites

In this study the effects of high temperature and moisture on the impact damage resistance and mechanical strength of Nextel 610/alumina silicate ceramic matrix composites were experimentally evaluated. Composite laminates were exposed to either a 1050°C isothermal furnace-based environment for 30 consecutive days at 6 h a day, or 95% relative humidity environment for 13 consecutive days at 67°C. Low velocity impact, tensile and short beam strength tests were performed on both ambient and environmentally conditioned laminates and damage was characterized using a combination of non-destructive and destructive techniques. High temperature and humidity environmental exposure adversely affected the impact resistance of the composite laminates. For all the environments, planar internal damage area was greater than the back side dent area, which in turn was greater than the impactor side dent area. Evidence of environmental embrittlement through a stiffer tensile response was noted for the high temperature exposed laminates while the short beam strength tests showed greater propensity for interlaminar shear failure in the moisture exposed laminates. Destructive evaluations exposed larger, more pronounced delaminations in the environmentally conditioned laminates in comparison to the ambient ones. External damage metrics of the impactor side dent depth and area directly influenced the post-impact tensile strength of the laminates while no such trend between internal damage area and residual strength could be ascertained.     

Robust Metallic Actuators Based on Nanoporous Gold Rapidly Dealloyed from Gold–Nickel Precursors

Dealloyed nanoporous gold (np-Au) has applications as oxygen reduction catalysis in Li-air batteries and fuel cells, or as actuators to convert electricity into mechanical energy. However, it faces the challenges of coarsening-induced structure instability, mechanical weakness due to low relative densities, and slow dealloying rates. Here, monolithic np-Au is dealloyed from a single-phase Au₂₅Ni₇₅ solid-solution at a one-order faster dealloying rate, ultra-low residual Ni content, and importantly, one-third more relative density than np-Au dealloyed from conventional Au₂₅Ag₇₅. The small atomic radius and low dealloying potential of the sacrificing element Ni are intrinsically beneficial to fast produce high relative density np-Au, as predicted by a general model for dealloying of binary alloys and validated by experiments. Stable, durable, and reversible actuation of np-Au takes place under cyclic potential triggering in alkaline and acidic electrolytes with negligible coarsening-induced strain-shift. The thermal and mechanical robustness of bulk np-Au is confirmed by two-order slower ligament coarsening rates during annealing at 300 °C and 45 MPa macroscopic yielding strength distinctive from the typical early onset of plastic yielding. This article opens a rich direction to achieve high relative density np-Au which is essential for porous network connectivity, mechanical strength, and nanostructure robustness for electrochemical functionality.