Experimental and numerical study on compressive performance of perforated brick masonry after fire exposure

This paper discusses the compressive performance of perforated brick masonry after fire exposure. Compressive strength tests of the mortar, clay perforated brick, and perforated brick masonry specimens were performed in accordance with ISO834 fire tests of different durations. The temperature distribution of the masonry materials and specimens was simulated using the finite element software ABAQUS, with the thermal parameters of masonry materials recommended by European standard Eurocode 6 and related literature. The compressive strength reduction factors of mortar and clay perforated brick exposed to different fire durations were calculated via the layered method suggested by European standard Eurocode 1. In addition, the compressive strength reduction factors after cooldown were obtained from the experimental data of the masonry materials, and by considering further reductions in the compressive strength after cooling from high temperatures. Experimental data of the masonry specimens were compared with the numerical results obtained using the reduction factors proposed in this work. The comparison revealed an overall acceptable approximation. Thus, the method presented in this paper can be used to evaluate the residual capacity of masonry structures after fire.     

模铸用高铝质流钢砖的显微结构分析

选取市场上模铸用高铝质流钢砖与用后残砖作为研究对象,通过检测不同高铝质流钢砖的理化性能,对比其使用前后的显微结构变化,进一步探讨模铸过程中高铝质流钢砖的显微结构对钢铁产品质量的影响。结果表明:由于显气孔率较大、结构比较疏松、烧结不致密等特性,高铝质流钢砖在经受钢水冲刷时,钢水容易渗透至高铝质流钢砖内部,加速其损毁;其次,高铝质流钢砖与钢水发生物理化学反应后在其表面生成低熔点物,使钢水中产生夹杂物,影响钢铁产品的质量。     

Effect of waste serpentine on the properties of basic insulating refractories

Basic insulating refractories were fabricated by the pressing route using dead-burned magnesia, pure calcined alumina, expanded perlite, and calcined waste serpentine as starting raw materials in four compositions from F1 to F4. Periclase and forsterite were major phases in F1 and F2 compositions, while spinel was also detected in the XRD patterns of F3 and F4 samples. Quantitative phase analysis showed that F4 sample sintered at 1450?°C has the highest forsterite content among all other samples. On the other hand, it has lower thermal conductivity compared to F1 to F3, and even lower than aluminosilicate IFBs with the same bulk density. It is concluded that forsterite is a highly insulating material, compared to periclase, corundum, periclase-spinel, aluminosilicates, such as mullite, etc.     

正确选用热力管网保温材料的几个问题

介绍了做好热力管网保温应具备的有关知识和数据，以及宝钢蒸汽主干管网在采用四种保温材料下的经济保温层厚度和相对的节能效益，认为目前适于宝钢公司热源温度在６００℃以下较好的保温材料有新型矿渣棉制品和泡沫石棉板。     

底部两层框架-抗震墙砖房抗震能力的分析方法与设计控制

提出了底部两层框架 -抗震墙砖房框剪层和砖混层的极限受剪承载力、侧移刚度、极限剪力系数计算公式 ,并基于设置不同数量抗震墙的底部两层框架 -抗震墙砖房的实例计算和弹塑性时程分析 ,给出了结构砖混过渡层与相邻框剪层的极限剪力系数比和侧移刚度比的合理取值及薄弱楼层位置判别和破坏状态评定的方法和原则。     

钢包钢水保温覆盖剂的开发

研制了钢包钢水新型保温覆盖剂，主要成分为（%）；15-25C，20-35SiO2,10-20Al2O3,2-5Fe2O3,15-25CaO,2-5MgO，新覆盖剂铺展性与保温性能良好。经转炉钢水160t钢包生产使用，统计数据表明，镇静15min后钢水降温速度由原碳化稻壳覆盖剂1.33℃/min降低到0.93℃/min。     

混凝土多孔砖裂缝防治措施

分析了混凝土多孔砖墙体产生裂缝的原因,并详细阐述了混凝土多孔砖墙体裂缝的防治措施.     

转炉出钢口套整体袖砖工艺技术开发

介绍了天津天铁冶金集团有限公司炼钢厂转炉出钢口袖砖工艺的开发过程，主要工艺参数的制定，实践证明，该工艺的应用取得了良好的使用效果。     

提高中碳锰铁精炼电炉炉龄的实践

通过对精炼电炉炉体改造和出铁口材质、砖型的更新，解决了在中碳锰铁生产过程中炉眼易损问题，提高了炉龄，降低了生产成本。     

铝镁碳砖中三氧化二铝的测定

探讨了试样先灼烧除碳，再加混合熔剂副熔，盐酸溶液中浸取，采取氟盐置换法，测定铝镁碳砖中三氧化二铝，终点易于判断，结果令人满意。