Ce对共晶Mg-Al合金组织的影响

模拟AZ9l镁合金半固态液相凝固后期的成分，分析了共晶成分镁铝合金添加不同含量的稀土元素Ce后，铸态显微结构的变化。结果表明：Ce的加入改变了合金的组织，增加了初晶α相的含量，细化了β相并减少了β相的含量。随着稀土Ce加入量的增加，在Ce的加入量为0．6％时，所得的组织最好；在Ce含量大于0．6％时，随着Ce加入量的增加，细化效果反而变差。     

Partial Oxidation of Methane to Syngas over Calcined Ni–Mg/Al Layered Double Hydroxides

The catalytic partial oxidation of CH₄ to syngas was carried out over an Ni–Mg/Al mixed-oxide catalyst prepared from layered double hydroxide-type precursors. The catalysts were characterized by XRD, TPR, UV-DRS, XRF, BET and CHNS analysis. The effects of the catalyst composition and the calcination temperature on the catalytic performance and the extent of catalyst deactivation were investigated. Ni–Mg/Al oxide catalysts converted CH₄ into syngas efficiently with high selectivity. The catalyst performance was strongly related to the Ni particle size and the calcination temperature. The catalysts that were calcined at higher temperature exhibited a better catalytic performance. In conclusion, the NiAl₂O₄ spinel phase had a positive effect on the stability of the catalyst.     

硬脂酸柱撑类水滑石的制备及应用

采用离子交换法制备了硬脂酸柱撑类水滑石,并用红外光谱分析对其进行了表征.通过HAAKE流变仪、颜色测定仪研究了硬脂酸柱撑类水滑石与钙锌热稳定剂并用时的热稳定性,重点考察了水滑石的结构对PVC稳定性能的影响.结果表明硬脂酸柱撑类水滑石与钙皂/锌皂复配显著改善了PVC热老化过程中的初期着色性.     

镁铝水滑石及其复合体系对PVC热稳定性能的调控

采用比色法、热失重法等研究了不同镁铝摩尔比的水滑石(LDHs)对PVC糊热稳定性能的影响。结果表明,在镁铝比分别为2、3、4的样品中,镁铝比为2的LDHs对PVC的热稳定效果最佳;将其与传统的铅盐、有机锡稳定剂复配,均具有良好的协同效应,可以实现对PVC糊热稳定性能的控制。其中,PVC/Mg-AlLDHs/Sn以100∶1.5∶1.5(质量份数,下同)比例复合后的体系,不仅热稳定性能优于传统的的铅盐体系,而且具有较低的糊黏度及较好加工流变性能。     

镁铝合金阳极氧化表面处理工艺研究

研究了镁铝合金的阳极氧化过程,通过表面处理、化学清洗(脱脂除油)、碱蚀、化学抛光、电解着色、水合封孔、清洗和干燥等过程,得到符合国家标准的镁铝合金成品。     

Zn-Al-CO_3水滑石晶粒尺寸控制与光屏蔽作用研究

在旋转液膜反应器中制备成核浆液 ,通过控制晶化温度制备了不同粒径且晶体结构完整的Zn Al CO3水滑石 (LDHs)。将不同粒径的Zn Al CO3LDHs配成质量分数为 0 0 2 %的水分散液 ,测定在紫外 -可见光范围的透过率 ,结果发现 ,随晶化温度的升高 ,LDHs粒径增大 ,样品对紫外及可见光的阻隔作用增强 ;Zn Al CO3LDHs在不同波长下的吸光度与晶体粒子在a轴和c轴方向的尺寸呈线性关系。由外推法求得了Zn Al CO3LDHs对各波长紫外 -可见光产生屏蔽作用的晶粒尺寸阈值。对波长分别为 2 90、3 2 0、40 0、60 0和 80 0nm光波能够产生屏蔽作用的Zn Al CO3LDHs ,其粒子尺寸在a轴方向需分别大于 3 2 92、3 3 77、3 4 77、3 5 5 6、3 5 79nm ;在c轴方向需分别大于 9 73、12 79、16 47、19 3 5、2 0 2 2nm。     

室温超快速制备HKUST-1及其对甲苯的吸附性能

以硝酸铜和均苯三甲酸为原料,通过水滑石法室温10 s快速制备了一种金属有机骨架材料HKUST-1,对其进行了XRD、SEM和N_2吸附表征,测定了甲苯在HKUST-1上的吸附等温线、动力学和吸附-脱附循环性能。结果表明,水滑石的添加使HKUST-1可在室温10 s内快速合成,HKUST-1的BET比表面积达到2170.7 m~2/g,总孔容为0.97 cm~3/g。HKUST-1在25℃时对甲苯的饱和吸附量达到6.67 mmol/g,在低相对分压(p/p_0≈0.029)下,HKUST-1对甲苯的吸附量高于其他材料约10倍。经5次吸附-脱附循环后,HKUST-1的甲苯饱和吸附量几乎不变,具有很好的再生性能。     

First-principles Investigation of the Structural,Electronic and Elastic Properties of Al2Ca and Al4Sr Phases in Mg-Al-Ca（Sr） Alloy

First-principles calculations have been carried out to investigate the structural stabilities, electronic structures and elastic properties of Mg17Al12, Al2Ca and Al4Sr phases. The optimized structural parameters are in good agreement with the experimental and other theoretical values. The calculated formation enthalpies and cohesive energies show that Al2Ca has the strongest alloying ability, and Al4Sr has the highest structural stability. The densities of states （DOS）, Mulliken electronic populations, and electronic charge density difference are obtained to reveal the underlying mechanism of structural stability. The bulk modulus, shear modulus, Young＇s modulus, and Poisson＇s ratio are estimated from the calculated elastic constants. The mechanical properties of these phases are further analyzed and discussed. The Gibbs free energy and Debye temperature are also calculated and discussed.     

HEAT TREATMENT STRENGTHENING EFFECTS OF RARE EARTHS ON Mg—9Al ALLOY

Mg-9Al-xRE magnesium alloys were studied, where, x is 0, 0.4. 0.8. 1.2 and 1.6% (in weight percent, wt%), respectively. Influence of rare earths (RE) on microstructure and strength in both T4 (solute heat treatment) and T6 (solute heat treatment and artificial ageing treatment) were investigated. Strength of specimen was tested at ambient temperature. The micro structure was analyzed by optical microscopy, scanning electron microscopy (SEM) and X-ray diffraction analysis. RE additions improved T4 tensile strength of the treated alloys. Small addition (0.4wt%) of RE greatly improved the strength of ageing treated (T6) Mg-9Al alloy, but further additions caused decreasing.