0.89dtex细旦涤纶短纤维工艺优化探讨

介绍了纺制 0 89dtex× 3 8mm细旦涤纶短纤维的工艺技术特点 ,着重讨论了熔体温度、纺丝速度、冷却条件等工艺对原丝性能及产品质量的影响     

一步法生产涤纶FDY工艺的探讨

利用ＫＶ７３１纺丝设备一步法生产出涤纶ＦＤＹ，探讨了热辊拉伸和熔体温度对纤维质量的影响。采用高特性粘数的聚酯切片，严格控制纺丝工艺，可以在５０００ｍ／ｍｉｎ的纺丝速度下纺制高质量的细旦涤纶ＦＤＹ。     

PTT/PBT共混体系及可纺性探究

研究了PTT/PBT共混体系的相容性和结晶性能,并对体系的可纺性作了初步探究。结果表明:PTT/PBT共混体系在无定形区具有较好的相容性,但在晶区是晶相分离的。在冷结晶过程中,当PBT含量超过20%时,将促进体系的结晶性能;而在熔融结晶过程中,第二组分的加入抑制了体系的结晶性能,当配比为50/50时,结晶速率相对最低。另外,PTT/PBT共混体系表现出了良好的可纺性,共混纤维的断裂伸长率随着拉伸倍数和体系中PBT含量的增大而减小,强度增大,但稍差于纯组分纤维;当PTT含量达到50%后,共混纤维表现出了明显优于纯PBT纤维的回弹性,而当PTT含量达到70%时,共混纤维的回弹性能已接近纯PTT纤维。     

Rheological study on O−carboxymethylated chitosan/cellulose polyblends from LiCl/N,N‐dimethylacetamide solution

An O?carboxymethylated chitosan (O? CMCh) water solution (I) and N,N‐dimethylacetamide (DMAc) emulsion (II) were blended with a cellulose LiCl/DMAc solution, and corresponding polyblends (Polyblends I and II) were obtained. The rheology of the three fluids, that is, the cellulose solution and Polyblends I and II, was investigated. The cellulose solution was characterized by a power‐law fluid. When an O‐CMCh water solution or DMAc emulsion was added to the cellulose solution, the power‐law curve was preserved. The power‐law indexes (n) of all three fluids increased along with the temperature. Polyblend I displays an n close to but a little higher than that of the cellulose solution, while Polyblend II shows a much higher power index than those of the other two fluids. The values of the apparent viscosity (η_a) for all the three fluids are close and decrease along with an increase in the temperature. Adding O‐CMCh microparticles into Polyblends I and II results in a decrease in the structural viscosity index (Δη) in comparison to that of the cellulose solution, and this effect is very obvious for Polyblend I. A cellulose solution's Δη declines with the augmentation of temperature, while the Δη's of both Polyblends I and II show minimum values at about 323 K. © 2003 Wiley Periodicals, Inc. J Appl Polym Sci 88: 1719–1725, 2003     

Preparation,crystallization, and spinnability of poly(ethylene terephthalate)/silica nanocomposites

Poly(ethylene terephthalate) (PET)/silica nanocomposites were successfully prepared by in situ polymerization. Silica nanoparticles were uniformly dispersed in the process of polymerization. By means of hot‐stage polarization microscope and DSC, the influence of nanosilica on the crystallization of PET/silica nanocomposites has been clarified. The results show that nanosilica does not behave as a nucleating agent in PET but postpones the appearance of crystallite. This phenomenon is very favor to improve spinnability. The investigation on melt spinning of PET/silica nanocomposites also shows that it is advantageous to spinning with descending the spinning temperature. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 2564–2568, 2007     

仿真丝改性涤纶研究——Ⅱ.改性涤纶树脂可纺性

PET-SIPM和PET-SIPM-PEG改性涤纶树脂与纯PET树脂按一定的配比进行共混熔融纺丝,制得仿真丝改性涤纶。讨论了改性涤纶树脂的热性能和流变性能对其可纺性的影响,并对改性涤纶纺丝工艺控制及纤维的结构和性能进行了论述。研究表明,PET-SIPM/PET和PET-SIPM-PEG(M_n=200)/PET改性涤纶的可纺性与纯涤纶相匹敌,符合仿真丝纤维的要求。     

PET蓄光纤维的研制及性能研究

采用共混纺丝法制备了PET蓄光纤维,并对纤维的性能进行了研究。SEM分析表明,采用偶联剂可以有效地改善聚酯与蓄光粉体组成的共混体系的相容性,减小分散相颗粒的尺寸。预先将PET、蓄光粉体与偶联剂制备成母粒用于纺丝,可以明显提高体系的可纺性。同时,研究了蓄光粉体的含量对纤维力学性能和发光性能的影响。     

聚酯分子量分布对可纺性的影响

根据不同聚酯切片在常规指标相同的情况下可纺性往往不同，重点介绍用凝胶渗透色谱法和筛析色谱法对聚酯的低分子成分及分子量分布的检测研究，以及分子量分布对可纺性具有的重要意义。     

TiO_2表面改性对聚酰胺6纤维强度及染色性能的影响

将TiO2表面包覆无定形TiO2,再经复配偶联剂改性后,分散在己内酰胺-水体系中乳化,于聚合釜中水解开环聚合,得到全消光聚酰胺6(PA6)切片。PA6切片经熔融纺丝制得PA6全消光纤维,并织成PA6全消光织物。用热重分析仪、纳米激光粒度仪、沉降试验等研究了改性TiO2的性能及在己内酰胺-水体系中的分散性;用差示扫描量热仪、扫描电子显微镜等研究了PA6全消光纤维结晶性能和截面形貌。结果表明:经复配偶联剂改性的TiO2在树脂基体中有很好的分散性;PA6全消光纤维的可纺性好;加入改性的TiO2后,PA6纤维的强度提高了25%,但对PA6纤维的熔融温度没有影响;改性PA6全消光织物的上染率提高了10%。     

碳黑/聚酯复合纤维中导电组分的研究

以碳黑为导电介质，以PET为基体，用共混方法纺出共混导电纤维．研究表明，提高碳黑的分散性能提高共混体系的可纺性和导电性；并随着碳黑含量的增加，导电性提高；当碳黑含量达22％时，电阻为10^5Ω/cm，但可纺性和机械性能变差，此时，只适合于用作复合纤维的导电组分。