Failure analysis of a hot extrusion die used for Al-Li alloy processing

Al-Li alloys being developed as lighter, substitutes for conventional high strength Al alloys are to be processed by routine methods. During extrusion of a 8090 Al-Li alloy, the extrusion die container failed causing some alarm. This failed die container was analysed to examine if the failure was caused by interaction of Li diffusing out of Al-Li alloy with the carbides of die steel. The evidence, although not conclusive, is sufficient to exercise caution during such processing.     

微量Ag对CP276合金性能和组织的影响

研究添加不同含量的Ａｇ对ＣＰ２７６合金的拉伸性能和时效组织的影响。对拉伸强度、延伸率测试及透射电镜观察表明：０．１１ｗｔ％加入可促进Ｔ１相析出，使合金强度值升高；０．３５ｗｔ％Ａｇ的加入可在时效前期生成富Ａｇ、Ｍｇ的稳定的ＧＰ区，从而降低合金中Ｃｕ的固溶度，阻碍Ｔ１相析出，时效后期，ＧＰ区分解，生成大量Ｔ１相，使合金强度值显著升高。     

铝锂合金力学性能的各向异性

针对当前困扰铝锂合金实际应用的各向异性问题，概述关于铝锂合金中各向异性的表现规律，产生机理及对于降低各向异性所采用的方法等方面的研究现状和进展，对铝锂合金各向异性表现与微观组织结构的关系以及目前克服各向异性所采用方法的局限性进行分析。就此提出，若彻底解决这一问题则必须采用更先进的合金化方法及热加工工艺，研制新一代铝锂合金的观点和研究方向。     

2197铝锂合金的组织和性能

通过力学性能测试和显微组织观察研究了2197合金组织和性能之间的关系。结果表明,2197合金具有中等强度,小的各向异性,强的热稳定性。该合金在T8状态下能获得最佳的强度和塑性配合,在T6峰时效状态以析出少量δ′相、θ′相和T_1相联合强化为主。在2197合金的相组成中,T_1相析出数量不占主导地位,Al_6Mn弥散质点的析出有利于减小各向异性。2197合金中Li含量较低,使其呈现较强的热稳定性。     

钛在F—22先进战术战斗机上的应用

在Ａｌ－Ｌｉ二元单晶体的锯齿流变中，锯齿类型决定于加载的应变速率，与锯齿产生的临界应变随温度和应变速率的变化没有对应关系；锯齿序列中的应力幅度随时效时间的变化较大。     

快速凝固Al—Li—Mg—Zr合金粉末粒度对组织和性能影响

研究超音雾化快速凝固Al—Li—Mg—Zr合金粉末粒度对组织和性能的影响中发现,粉末粒度越细,组织越细,合金强度越大;但粒度太细,又会导致塑性变差。试验合金粒度范围选用40—100μm为佳。     

MICROSTRUCTURE AND MECHANICAL BEHAVIOUR OF Al-Li-Zr AND Al-Li-Cu-Mg-Zr ALLOYS

The aging response,tensile and impact properties of two kinds of Al-Li based alloys havebeen studied.The microstructure,deformation as well as fracture behaviour in the alloys wereobserved with SEM and TEM.It was found that the mechanisms of deformation and fracturefor different heat-treated alloys with the same chemical composition are quite different.Thecauses leading to the drop of ductility,toughness as well as anisotropy in peak-aged alloyshave been analysed.Finally,possible methods to improve the ductility and toughness of the al-loys have been discussed.     

铝-锂合金腐蚀性能研究综述

综述了铝-锂合金孔蚀、晶间腐蚀、应力腐蚀断裂(SCC)及剥蚀的研究现状。阐述了加工状态、热处理、显徽组织及腐蚀介质对一些铝-锂合金孔蚀及晶间腐蚀行为与SCC敏感性的影响及其影响机制．同时报道了一些研究铝-锂合金剥蚀的新方法，并提出了进一步研究的方向．     

热力耦合作用下Al-2.8%Cu-1.35%Li-0.11%Zr合金析出相演化和力学性能

通过TEM、HAADF-STEM和室温拉伸实验开展Al-2.8%Cu-1.35%Li-0.3%Mn-0.11%Zr合金在人工时效和蠕变时效状态下的析出相演化规律和力学性能研究。结果表明,160 ℃时效条件下,人工时效和160 MPa应力时效过程中合金中析出相数量均随时效时间的延长而增多,相同时效时间条件下应力时效状态合金T₁相数量较多,但其平均直径减小了约5~15 nm。这主要是因为外加应力增加了合金中的位错密度从而促进析出相析出。T₁相在时效析出过程中并未受外加应力的影响而沿某个方向择优析出,无明显的应力位向效应,这可能与T₁相具有更大的惯习平面变体上的形核与临界应力值有关。相比于人工时效,应力时效后合金的室温屈服强度和抗拉强度均增加,且在时效初期对屈服强度效果更为显著。      

预形变和时效Al-2.73Li合金的断裂机制SCIEI

本文研究了预先冷形变对Al-2.73Li合金的机械性能和断裂行为的影响。试验结果表明,预先冷形变使合金的加工硬化率和强度提高,相应损失部分塑性。预先冷形变造成不均匀分布的胞状位错结构及晶界无沉淀带加工硬化,乃是导致塑性下降的主要原因。合金的断裂方式为沿晶和穿晶混合型。预形变后时效使沿晶断裂倾向增大。最后探讨了其断裂机制。