Pressure-induced transparency of MgO,Al2O3, AlN,and cBN ceramics at room temperature

The in situ axial X-ray diffraction patterns of four ceramic powder samples (MgO, Al₂O₃, AlN, and cBN) that were compressed in a diamond anvil cell under uniaxial non-hydrostatic conditions were recorded. The microscopic deviatoric stress as a function of the pressure was determined from the X-ray diffraction peak broadening analysis: the curves increased approximately linearly with the pressure at the initial compression stage and then levelled off under further compression. Pressure-induced transparency was observed in all of the samples under compression, and the pressure at the turning point on the curves of the microscopic deviatoric stress versus pressure corresponded to the pressure at which the samples became transparent. Analysis of the microstructural features of the pressure-induced transparent samples indicated that the compression caused the grains to fracture, and the broken grains bonded with each other. We demonstrated that the ceramics’ pressure-induced transparency was a process during which the grains were squeezed and broken, the pores were close between the grains, and the broken grains were re-bonded under compression.     

Grain size effect on microwave dielectric properties of Na2WO4 ceramics prepared by cold sintering process

In this work, cold sintering was adopted to prepare Na₂WO₄ ceramics with different grain sizes ranging from 0.632 μm to 17.825 μm. Their microstructures, complex impedance, and microwave dielectric properties were studied in-depth. It was found that samples with relative densities higher than 92% can be successfully synthesized by cold sintering process at a low temperature of 240 °C. However, their electrical properties have strong dependence on the grain size. Specifically, the resistance of grain boundaries decreases dramatically with the increase of grain sizes, while the quality factor has a positive correlation with the grain sizes of Na₂WO₄ ceramics. Excellent microwave dielectric properties, including permittivity = 5.80, Q × f = 22,000 GHz, and TCF = −70 ppm/°C, are obtained for Na₂WO₄ ceramics with a grain size of 4.477 μm prepared by cold sintering process.     

寒冷地区某既有办公建筑围护结构优化改造研究

既有公共建筑能耗中,围护结构节能潜力巨大。以兰州某既有办公建筑为例,采用DeST-C软件模拟围护结构不同材料厚度、窗型,得出系列负荷,通过对数据分析、比较,得出如下结论:外墙外保温适宜材料为50mm的挤塑板,最大热负荷节能率为45.66%;屋面适宜保温材料为65mm的挤塑板,最大热负荷节能率为4.25%;外窗各个朝向全部更换玻璃,推荐选用内张膜中空玻璃(双膜),最大热负荷节能率为7.36%;单独更换南向外窗材料,推荐选用真空镀膜复合中空玻璃,最大热负荷节能率为1.78%。     

风机主轴锻件锻后热处理工艺优化

通过对42CrMo4风机主轴结构尺寸、性能要求、材质特点等方面进行分析,对原有锻后热处理工艺进行优化,制定出既能达到锻后热处理效果又经济节能的工艺参数。     

Automated and Continuous Production of Microstructured Metallic Plates via Cold Embossing

Many critical issues need to be addressed when microstructured reactors are manufactured in large unit volumes. The most crucial of these are cost, ease of production, and reliability. The lack of breakthrough manufacturing technology to provide high‐efficiency, low‐cost, high‐precision plates is a hindrance to the early market implementation of systems requiring metallic microstructured plates. This contribution focuses on the development and optimization of a combined embossing and bending tool for the quick and continuous manufacture of easily machined plates.     

浅析HPT250轧机中滑移系数对轧制过程的影响

通过HPT250轧机在技术改造中遇到的一个问题，即滑移系数对冷轧元缝钢管在轧制过程中所起的作用。在实际生产中经过不断的技术研究和改进。使闲置多年的HPT250轧机为钢管公司的生产迭拉起到很大的作用。     

低温送风系统末端装置诱导器的研究及性能评价

研究了在低温送风系统中诱导器(IDU)的结构特点、工作原理、送风方式,分析了诱导器送风口射流速度的特性,得出了诱导器空调系统的优缺点。     

低温脂肪酶产生菌的筛选、鉴定及其部分酶学性质

从南极乔治王岛冻土来源的76株低温细菌中筛选到13株低温脂肪酶产生菌，对其中的BTsl0022菌株进行鉴定。通过生理生化特征、16s rDNA基因序列的同源性和系统发育分析发现，菌株RTsl0022属于假单胞菌属(Pseudomonas)，但与已定名的假单胞菌有一定的差异，与未定名的Pseudomonas sp．PsB的亲缘关系最接近，故将其暂定名为Pseudomonas sp．BTsl0022。对该菌脂肪酶的酶学性质初步研究表明，酶的最适作用温度为24℃，对热敏感，60℃处理30min仅残留25％酶活性，酶的适宜作用pH范围在7．0～9．0，最适pH为8．0。     

大型连杆流线简易试验方法

介绍了一种大型连杆流线的简易试验方法及其评价原则。该方法可清晰显示流线，并适合任何尺寸和形状的锻造连杆的流线试验。