Impact of gypsum on flotation of scheelite and fluorite using sodium oleate as collector

ABSTRACT

In this study, effect of calcium and gypsum on scheelite and fluorite was investigated using sodium oleate as collector. Micro-flotation and contact angle results showed that the adsorption of calcium could inhibit the hydrophobicity of scheelite and fluorite. Moreover, sulfate could enhance the inhibition. FT-IR results showed that calcium could be priori precipitated into calcium oleate and adsorb on mineral surface. The adsorption of calcium could increase the scheelite potential to IEP, while it showed limited effect on fluorite potential. However, the interaction of calcium on scheelite and fluorite in gypsum solution was more complex than that in calcium solution.     

稀土石膏常压酸化法制备硫酸钙晶须的研究

以含稀土的石膏为原料运用常压酸化法合成硫酸钙晶须,探讨了不同工艺条件对生成的硫酸钙晶须形貌的影响,同时还考察了晶型助长剂的种类和晶型助长剂的含量对硫酸钙晶须生长的影响,利用SEM和XRD分别对硫酸钙晶须的表面形貌、物相特征做了表征分析。实验得到制备硫酸钙晶须的最佳的反应条件：稀土石膏质量浓度为0.22 g/mL、反应时间为25 min、盐酸浓度为2.8 mol/L、反应温度为70 ℃、陈化时间为4 h,在此条件下合成的硫酸钙晶须平均长度为61 μm,平均长径比为30.5;通过对比实验选出了CuCl₂作为促进硫酸钙晶须生长的助长剂,在添加5%（质量分数）的CuCl₂的情况下可使硫酸钙晶须长径比从30.5增至41,长度从61 μm增至81 μm。     

复合外加剂改性盐石膏的研究

盐石膏的主要成分为无水硫酸钙,其活性差、凝结硬化慢、强度低,需要添加活性剂来激发盐石膏的活性。通过复合外加剂对盐石膏加以改性,并通过XRD和SEM对其作用机理做了分析。结果表明,单掺脱硫石膏和建筑石膏均能缩短盐石膏的凝结时间,建筑石膏的效果较好,但掺量不宜过高。复掺建筑石膏和缓凝剂时,两者比例要控制得当,适宜的建筑石膏和缓凝剂掺量分别为50%和0.10%~0.12%（质量分数）。分析可知,大掺量建筑石膏会增加盐石膏硬化体中二水相和针棒状晶体的含量;缓凝剂掺量的增加,会降低盐石膏硬化体中二水相的含量,棱形晶体增多,从而降低了盐石膏的强度。     

石膏转化制硫酸钾结晶动力学及结晶添加剂研究

研究了浓氨介质中石膏与氯化钾直接转化制硫酸钾的结晶动力学及结晶添加剂的作用效果。结果表明 ,硫酸钾在氨介质中的成核速率与晶体生长速率、悬浮密度、搅拌速率存在如下关联式 :B0 =5 .64 13×10 8G3.32 0 8Mt0 .0 559np0 .2 92 8。加入异丙醇、OP乳化剂及十二烷基苯磺酸钠等添加剂 ,可使硫酸钾结晶产品纯度提高 ,晶体形态整齐均匀     

Continuous precipitation of calcium sulfate dihydrate from waste sulfuric acid and lime

Precipitation of calcium sulfate dihydrate, gypsum, from (i) a pure sulfuric acid/lime suspension and (ii) a waste sulfuric acid/lime suspension in a continuous pilot plant in the temperature range from 40 °C to 80 °C was studied. It was observed that in the case of waste sulfuric acid with a high content of Mg²⁺ and Fe²⁺ ions, several hours after the beginning of the precipitation, partial dissolution of the product and modification of the crystals from needle‐ and plate‐like to agglomerated structures occurred. It is suggested that the secondary changes occur due to the increased concentration of Mg²⁺ and Fe²⁺ ions in the reactor. Below 60 °C, and above 70 °C plate‐like and needle‐like single crystals respectively were formed. The mean size (d₅₀) of the crystals was found to increase with increasing temperature and decrease with the initial concentration of lime. Gypsum produced between 70 °C and 80 °C is suitable for further processing for construction plaster. In a precipitation process with pure sulfuric acid only single perfect needle‐like crystals occurred. Copyright © 2005 Society of Chemical Industry     

膏盐岩地层地质特征与录井技术

石油勘探实践和研究结果表明，许多油气藏的形成都与膏盐岩地层有关，也常与膏盐岩地层伴生，成功钻穿膏盐岩地层是钻井难题之一，录井技术成为钻进安全监测、膏盐岩地层准确预报的重要手段。针对上述情况，介绍了膏盐岩地层的主要类型、沉积模式以及与油气的关系，归纳总结了膏盐岩地层的录井技术经验，包括：在随钻录井过程中熟悉地质设计与邻井资料；在没有预测钻遇膏盐岩地层的情况下，通过钻井液中Cl^-的变化判定是否钻遇膏盐岩地层；预计钻遇膏盐岩地层时，使用饱和盐水钻井液；钻遇膏盐岩地层后观察盐岩是否以岩屑形式返出；同时，把握膏盐岩地层的岩性、岩性组合、层位、顶底界和厚度是非常重要的。通过S1井实例分析，论述了在膏盐岩地层中钻进时，防卡、防漏是录井人员监测和预报的重点。     

难处理金矿石加石灰焙烧焙砂中CaS的消除

介绍了用空气氧化预浸加石灰焙烧焙砂中的CaS，以消除其对金氰化的影响。预浸后金的氰化浸出率可从58％提高到80％以上。     

Observation and Analysis of Gypsum Particleboard using SEM

The microstructures of gypsum board and gypsum particleboard were observed by SEM. The effects of retarder and waterproof agent on the shape and the average dimension of the gypsum crystal were discussed. The mechanism was investigated as well. Four typical instances, i e, the gypsum crystal shape, the gypsum combined with particles on the particles surface, the gypsum combined with particles on the wood cross section and the gypsum combined with particles inside the wood cell cavity were selected and observed. Furthermore, the agglomeration and cementation mechanism between gypsum and particle were studied.     

亚硫酸钙氧化为石膏的研究

进行了亚硫酸钙氧化为二水石膏的研究 ,考察了初始 p H值、反应温度、空塔气速、固含量和停留时间对氧化率的影响 ,给出了适宜的反应条件 .在这些条件下 ,氧化率达 96 %以上     

石膏制品防水防潮剂的研制与开发

本文提出采用高分子有机材料配合，生产石膏制品防水防潮剂的生产方法和工艺。该剂还可以应用到氧化镁系列板材，同时提出开发珠光或彩色防水防潮剂，能达到满足的装饰效果，值提开发推广。