Preparation of CaO granules using the granulation method

ABSTRACT

Improving the hydration resistance of CaO particle in manufacturing and application of free CaO-containing materials has practical significance. In this study, CaO granules was made from Ca(OH)₂ particles, which were fabricated by the granulation method. The results showed that the hydration resistance of the CaO granules which was prepared under 1700?r?min^?1 was the best, the CaO granules was sintered well in calcination process, the shell of CaO granules was relatively dense, which improves the hydration resistance of CaO granules, and the rate of hydration weight increment was 0.58% after placed in the air for 20 days under a temperature of 10–14°C and a relative humidity of 57–81%.     

载体比表面积及孔径对Nb_2O_5/α-Al_2O_3催化剂酸性及反应性能的影响

采用浸渍法制备了Nb2O5/α-A l2O3催化剂(简称催化剂)并用于环氧乙烷水合制乙二醇的反应,通过控制α-A l2O3载体中致孔剂的含量来调变载体的孔径、孔分布及比表面积;采用吡啶吸附红外光谱、氨程序升温脱附法研究了载体的比表面积及孔径对催化剂酸性及反应性能的影响。实验结果表明,产物的选择性受扩散因素及催化剂酸性的影响,而催化剂的酸量、酸密度可以通过载体的孔径及比表面积的变化加以调控。比表面积较小及孔径较大的载体对催化剂催化环氧乙烷水合制乙二醇的反应较为有利。当载体的比表面积小于0.80m2/g、孔径为4.00~8.00μm时,在反应温度160℃、反应压力1.5M Pa、n(H2O)∶n(EO)=22、液态空速25h-1的条件下,环氧乙烷的转化率大于99.8%,乙二醇的选择性超过89.9%。     

溶剂对环氧乙烷催化水合制乙二醇的影响

研究了NY催化剂催化环氧乙烷水合制乙二醇(EG)过程中,溶剂、催化剂添加量和水与环氧乙烷的摩尔比(简称水比)对EG选择性的影响。实验结果表明,以丙三醇作为溶剂使催化剂进行循环,能提高EG的选择性,效果好于以生成的EG作为溶剂循环催化剂。催化剂添加量、水比和溶剂添加量对EG选择性具有较大影响,其中溶剂添加量对EG选择性的影响最显著。在低水比(1.0~4.0)条件下,EG质量分数小于30%、催化剂质量分数大于7.2%时,EG选择性稳定在95.63%~97.92%,平均值为96.80%,此结果对于进一步降低EG合成工艺的能耗具有指导意义。     

丙烯醛制备1,3-丙二醇的中型试验研究

对丙烯醛水合、加氢制1，3-丙二醇工艺进行了中试研究，主要对小试技术的可靠性进行验证。结果表明，丙烯醛经水合、加氢制1，3-丙二醇的工艺技术可行，反应器、精馏塔等设备设计合理。中试丙烯醛水合单程转化率为45％～55％，3-羟基丙醛选择性达到了93％左右，3-羟基丙醛加氢收率接近100％，产品1，3-丙二醇的醛基质量分数降至5μg／g以下。与小试结果相比较，中试的水合选择性明显提高，加氢催化剂活性寿命延长。     

夏季施工中砼质量存在问题与对策

分析了夏季砼施工中存在的突出问题 ,并论述了质量保证措施。     

Membrane Packaging System to Permit Safe Hydration of Freeze-Dried Contents with Impure Water

We tested the feasibility of using polymer membranes for a self-hydrating packaging system to reconstitute freeze-dried foods using nonpurified water. Several commercial membranes were screened according to (1) hydration rate, (2) water permeability, (3) passage of microorganisms, (4) salt rejection, and (5) strength. The most promising membranes were used for developing and testing prototype packaging systems. A feasible self-contained rehydration system was a nylon-6 polyamide membrane that rehydrated the freeze-dried food within 30 min while passage of microorganisms was prevented. The temperature was 37°C, and the food contained 0.5g/5g of a low molecular weight solute (salt). Such self-contained membrane rehydration systems must be designed to accommodate expected environmental conditions such as temperature, relative humidity, and nature of the product.     

乙二醇合成工艺的研究进展

对国内外乙二醇合成的传统工艺:直接水合法、催化水合法和碳酸乙烯酯法进行了介绍;对乙二醇合成的新工艺,包括乙二醇和碳酸二甲酯联产法和C1化学法的工艺流程和发展前景进行了综述,其中,C1化学法主要分为乙烯合成法、合成气合成法和甲醛、甲醇合成法。作为合成气合成法之一的合成气偶联合成法,具有工艺要求不高、反应条件温和等优点,是目前最有希望大规模工业化生产乙二醇的工艺路线。     

长垣东部深井井壁失稳及技术对策

大庆油田在长垣东部深层油气田勘探开发过程中存在井眼不稳定问题。在对深层失稳井段资料调研的基础上，开展了易塌地层泥页岩水化膨胀及分散特性评价以及比亲水量研究。通过泥页岩--试液模拟作用的化学位差反渗透实验以及压力传递实验等，探讨了不同条件下泥页岩水化应力变化规律。利用井壁稳定性模拟实验装置（SHM仪），评价了不同钻井液防塌效果。理论分析和实验表明，当使用水基钻井液在复杂泥页岩地层钻进时，如何控制泥页岩压力传递和流体侵入是解决泥页岩井壁不稳的技术关键。使用长垣东部深层泥页岩与硅酸盐钻井液作用的实验表明，硅酸盐钻井液能显著降低泥岩渗透率，阻止钻井液滤液与孔隙压力的传递，改善膜效率，有助于充分发挥化学位差诱导的反渗透防塌作用效果。     

大体积混凝土施工的监理实践

本文结合厦门和平里酒店工程基础施工的监理过程,介绍在大体积混凝土施工的监理工作中所采取的预控措施和质量控制方法