The structure,vacancy characteristics,and magnetic properties of GdMn1-xCrxO3 ceramics

To investigate the evolution of the structural and enhanced magnetic properties of GdMnO₃ systems induced by the substitution of Mn with Cr, polycrystalline GdMn_1-xCr_xO₃ samples were synthesized via solid-state reactions. XRD characterization shows that all GdMn_1-xCr_xO₃ compounds with single-phase structures crystallize well and that Cr³⁺ ions entering the lattice sites of GdMnO₃ induce structural distortion. SEM results indicate that the grain size of the synthesized samples (a few microns) decreases as the Cr substitution concentration increases. Positron annihilation lifetime spectroscopy reveals that vacancy-type defects occur in GdMn_1-xCr_xO₃ ceramics and that the vacancy size and concentration clearly change with the Cr content. The temperature and field dependence of the magnetization curves show that Cr substitution significantly influences the magnetic ordering of the gadolinium sublattice, improving the weak ferromagnetic transition temperature and magnetization of GdMn_1-xCr_xO₃. The enhanced magnetization of GdMn_1-xCr_xO₃ is closely related to the vacancy defect concentration.     

Facile synthesis of Ti3C2 MXene-modified Bi2.15WO6 nanosheets with enhanced reactivity for photocatalytic reduction of Cr(VI)

Through a facile hydrothermal method, we have successfully prepared Ti₃C₂/Bi_2.15WO₆ (TC/BWO) composite, and systematically investigated their reactivity for the photocatalytic reduction of Cr(VI) under visible light. X-ray diffraction and Raman analysis confirm the formation of heterostructure between Bi_2.15WO₆ and Ti₃C₂. The resultant 7TC/BWO composite exhibits enhanced photoactivity toward Cr(VI) reduction. After 120 min irradiation, the conversion of Cr(VI) reaches 92.5% with the quasi-first-order kinetic constant of k = 0.0145 min^?1, which is higher than that of pure BWO (30% and k = 0.0005 min^?1). The electrochemical and photoluminescent characterization confirm that the introduction of Ti₃C₂ is conducive to the separation of carriers, thus significantly improves the photocatalytic performance of TC/BWO. Furthermore, the radical capture experiments verify that the electrons are important for enhancing reduction of Cr(VI) to Cr(III). As a result, this research provides a comprehensive understanding of the reduction of Cr(VI) by TC/BWO composite under visible light.     

One step method of structure engineering porous graphitic carbon nitride for efficient visible-light photocatalytic reduction of Cr(Ⅵ)

Porous g-C3N4 nanosheets (PCN) were prepared by the nickel-assisted one-step thermal polymerization method.Hydrogen (H2) which was produced by the reaction between nickel (Ni) foam and ammonia (NH3) defined the structure and properties of PCN.During the formation of PCN,the participation of H2 not only enhanced the spacing between layers but also boosted the specific surface area that more active sites were exposed.Additionally,H2 promoted pores formation in the nanosheets,which was beneficial to the transfer of photons through lamellar structure and improved the absorption efficiency of visible light.Remarkably,the obtained PCN possessed better Cr(Ⅵ) photocatalytic reduction efficiency than pure g-C3N4.The reaction rate constant (k) of PCN (0.013 min-1) was approximately twice that of bare g-C3N4 (0.007 min-1).Furthermore,the effects of original pH and concentration of Cr(Ⅵ)-containing solution on removal efficiency of Cr(Ⅵ) were explored.A possible photocatalytic mechanism was proposed based on the experiments of radical scavengers and photoelectrochemical characterizations.     

30Cr13不锈钢冶炼过程夹杂物控制技术

  针对30Cr13生产过程中存在的轧材非金属夹杂物合格率偏低仅85%左右的问题，通过对30Cr13不锈钢精炼过程钢中非金属夹杂物存在形态进行分析，并结合现有精炼工艺制度，在实验室研究的基础上制定了不锈钢精炼过程非金属夹杂物控制方案。工业应用后，精炼结束钢中大于5 μm的非金属夹杂物总数、形状以及尺寸等参数均得到了有效改善，钢水洁净度大大提高。     

伞帽用高铬铸铁在热强碱腐蚀环境下的磨损分析

针对氧化铝行业中常用的Cr28和Cr20高铬铸铁伞帽在相同工况条件下的磨损机理进行分析,并对比研究了实际生产中两种失效材料的成分、组织及性能。结果表明,伞帽部件在高温强碱腐蚀条件下受到外界冲刷时,磨损量由微切削磨损与变形磨损这两种机制共同决定。含铬量较高的Cr28高铬铸铁,其冲刷和抗腐蚀磨损性能均优于Cr20高铬铸铁。伞帽服役寿命主要受浆料和表层的铸铁材料两大因素影响。两种试验材料经淬火+回火处理后,基体组织中主要为回火马氏体+M₇C₃型碳化物+少量残留奥氏体,其中含铬量较高的Cr28高铬铸铁中共晶碳化物含量更高,且分布更加弥散,其平均硬度值为64.0 HRC,高于Cr20高铬铸铁的60.2 HRC。最终确定Cr28高铬铸铁作为伞帽材质更能满足氧化铝生产及设备检修周期的需要。     

柱塞卡滞原因分析

某柱塞泵工作中发生柱塞卡滞,经显微形貌观察、光谱分析、电子探针面扫描分析和显微硬度分析等,确定柱塞卡滞的根本原因为原材料组织中存在严重的网状共晶碳化物,降低了强度和韧性,增大了柱塞球面表层的脆性,进而导致了球面部位的接触疲劳抗力下降。严重的疲劳磨损与接触疲劳造成了柱塞球面脱层破坏,由此产生的金属碎屑进入柱塞与衬套的配合间隙处,进而限制了柱塞的自由运动。     

咖啡渣活性炭的制备、表征及其对Cr(Ⅵ)的吸附机制研究

以碘吸附值为评价指标，活化时间、活化温度和浸渍比为影响因素，采用响应面法试验设计对磷酸活化法制备咖啡渣活性炭的工艺条件进行优化，并通过静态吸附试验研究了不同吸附时间、溶液pH值和吸附温度条件下，活性炭对水溶液中Cr（Ⅵ）吸附性能的影响，最后利用Langmuir、Freundlich吸附等温方程、准一级动力学方程、准二级动力学方程和颗粒内部扩散方程进行拟合。试验结果表明，制备咖啡渣活性炭的最佳工艺条件为活化时间1 h、活化温度498℃、浸渍比1.72；在此条件下活性炭得率为30.4%，碘吸附值为（799±16）mg/g，比表面积为1 006 m²/g，孔容为0.779 cm³/g、微孔孔容为0.051 cm³/g、平均孔径为3.088 nm。较低pH值和较高温度能够促进活性炭对Cr（Ⅵ）的吸附；Langmuir等温方程能够更好地描述活性炭对Cr（Ⅵ）的吸附效果；活性炭对Cr（Ⅵ）的吸附分3个阶段：快速吸附阶段、慢速吸附阶段和吸附平衡阶段，10 min内可完成吸附总量的79%，360 min内达到吸附平衡，该吸附过程符合准二级吸附动力学方程。分析表明咖啡渣活性炭对Cr（Ⅵ）的吸附主要为单分子层的化学吸附。     

Corrosion resistance of Al–Cr-slag containing chromium–corundum refractories to slags with different basicity

Al–Cr slag is the solid waste generated by the smelting of Cr metal. It presents a range of environmental hazards. This study addressed the corrosion resistance of Al–Cr slag containing chromium–corundum refractories to slags with different basicity. Herein, we provide suggestions for the use of Cr–corundum of different basicity in kilns. Al–Cr slag, brown fused Al₂O₃, and chrome green were used as the raw materials, with pure calcium aluminate cement being used as a binder. The brick samples, prepared using different blends of chrome green and corundum, were fired at 1600?°C, and subsequently subjected to a slag corrosion test. After corrosion by slag of different basicity, the phase composition and microstructure of the sample were analyzed by X-ray diffraction, energy dispersive spectrometer and scanning electron microscopy. There were two major findings. First, Cr–corundum brick made from Al–Cr slag has a better slag corrosion resistance than that made from Cr₂O₃ and brown fused Al₂O₃. Second, Cr–corundum brick made from Al–Cr slag has superior corrosion resistance to slag with a CaO:SiO₂ ratio of 2:1.