Low temperature sintering and microwave dielectric properties of (Mg0.7Zn0.3)0.95Co0.05TiO3 ceramics with BaCu(B2O5) additions

The effects of BaCu(B₂O₅) additives on the sintering temperature and microwave dielectric properties of (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics were investigated. The (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics were not able to be sintered below 1000 °C. However, when BaCu(B₂O₅) were added, they were sintered below 1000 °C and had the good microwave dielectric properties. It was suggested that a liquid phase with the composition of BaCu(B₂O₅) was formed during the sintering and assisted the densification of the (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics at low temperature. BaCu(B₂O₅) powders were produced and used to reduce the sintering temperature of the (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics. Good microwave dielectric properties of Q × f = 35,000 GHz, ?_r = 18.5.0 and τ_f = −51 ppm/°C were obtained for the (Mg_0.7Zn_0.3)_0.95Co_0.05TiO₃ ceramics containing 7 wt.% mol% BaCu(B₂O₅) sintered at 950 °C for 4 h.