MBE growth and characterization of in situ arsenic doped HgCdTe

We report the results of in situ arsenic doping by molecular beam epitaxy using an elemental arsenic source. Single Hg_1−xCd_xTe layers of x ∼0.3 were grown at a lower growth temperature of 175°C to increase the arsenic incorporation into the layers. Layers grown at 175°C have shown typical etch pit densities of 2E6 with achievable densities as low as 7E4cm⁻². Void defect densities can routinely be achieved at levels below 1000 cm⁻². Double crystal x-ray diffraction rocking curves exhibit typical full width at half-maximum values of 23 arcsec indicating high structural quality. Arsenic incorporation into the HgCdTe layers was confirmed using secondary ion mass spectrometry. Isothermal annealing of HgCdTe:As layers at temperatures of either 436 or 300°C results in activation of the arsenic at concentrations ranging from 2E16 to 2E18 cm⁻³. Theoretical fits to variable temperature Hall measurements indicate that layers are not compensated, with near 100% activation after isothermal anneals at 436 or 300°C. Arsenic activation energies and 77K minority carrier lifetime measurements are consistent with published literature values. SIMS analyses of annealed arsenic doping profiles confirm a low arsenic diffusion coefficient.