The self-assembling and application of inorganic antibacterial material made of natural nanoporous carrier |
| |
| Authors: | Chunbao Sun Beihai Zhou Hao Ding Dongdong Zeng |
| |
| Affiliation: | (1) School of Civil and Environmental Engineering, University of Science and Technology Beijing, Beijing, 100083, China;(2) School of Material Science and Technology, China University of Geoscience(Beijing), Beijing, 100083, China;(3) Institute of Process Engineering, Chinese Academy of Sciences, Beijing, 100080, China |
| |
| Abstract: | ![]()
The inorganic antimicrobial material was inhibited to the microbes with the added metal ion,Zn.The primary wet product carrying 5%-10% zinc ion was generated under the following conditions:temperature was 95℃,solution zinc concentration was 1.2-2.0 mol/L,and the ratio of Zn solution to zeolite weight was 5:1.The final stable product was manufactured after baking in an oven for 1-3 h at the temperature of 500-900℃.The baked material was tested for its disinfection effectiveness and coloring effect when mixed with paint coating.Based on the final batch of tests,the zinc content of this anti-microbial product was further optimized. |
| |
| Keywords: | inorganic antimicrobial nanoporous material antibacterial coating zeolite self-assembling |
| 本文献已被 维普 万方数据 SpringerLink 等数据库收录！ |
|