金属骨架材料MIL-53(Cr)合成及其吸附效果研究

采用新配比(n(Cr3+):n(H2BDC):n(H2O)=1:2:280),水热法合成MOFs材料MIL-53(Cr).材料后处理过程采用溶剂置换法.通过XRD、TG、SEM、IGA的表征手段对不同条件下合成后MIL-53(Cr)产物进行结构表征;通过N2、CO2、CH4、C2 H4、C2 H6单组份气体吸附实验对样品的吸附性能进行测试.结果显示:新的制备方案在制备过程中能够更稳定地合成出高纯度的MIL-53(Cr)产物,溶剂置换的后处理方法能够有效的将孔道内H2BDC除去,经过后处理MIL-53(Cr)比表面积为1355.9 m2?g?1,通过初步的气体吸附实验表明该材料具有广阔的应用前景.

Preparation of Metal-Organic Frameworks MIL-53(Cr) and its Absorption Perfomance

MIL-53(Cr),was hydrothermally synthesized under new reaction conditions(1:2:280).Solvent-replacement was used during the post treatment of MIL-53(Cr).The synthesized MIL-53(Cr) was characterized by XRD,TG,SEM and IGA,respectively,and its absorption performance was examined by the experiments of pure gas absorptions of N2,CO2,CH4,C2H4 and C2H6,respectively.The results show that using the new recipe can make the preparation of MIL-53(Cr) more stable,and the solvent-replacement method can remove the impurities from the porous channels of the MIL-53(Cr) almost completely and make the prepared MIL-53(Cr) with high purity.After post treatment,the specific surface area of the MIL-53(Cr) is 1355.9 m2?g?1,and via a series gas absorption experiments,the prepared MIL-53(Cr) shows a broad prospect in different applications.