Effects of Silver Doping on the Sol–Gel-Derived Ba4(Nd0.7Sm0.3)9.33Ti18O54 Microwave Dielectric Ceramics

Tungstenbronze-type Ba₄(Nd_0.7Sm_0.3)_9.33Ti₁₈O₅₄ (BNST) microwave dielectric ceramics doped with 0–10 wt% silver (Ag) particles were successfully fabricated by a citrate sol–gel method. The influence of Ag doping on the sinterability, microstructure, bulk conductivity, and dielectric properties of BNST was investigated. The desired tungstenbronze-type phase was obtained at 900°–950°C. The sintering temperature of BNST decreased to 1100°C with the aid of a small amount of Ag addition (1 wt%). No chemical reaction between the tungsenbronze phase and Ag was detected. The particle size of the powders decreased with increasing Ag content up to 1 wt% and it then increased with a further increase in the Ag content. The dense fine-grained ceramics with submicrometer grains (～300 nm) were obtained with 1 wt% Ag addition. The submicrometer-grained ceramics had excellent dielectric properties of ?_r～81 and Q × f ～11 000 GHz. Both the dielectric constant and dielectric loss significantly increased with large additions (>3 wt%) of Ag due to the percolation effect.