Fabrication and electrical characteristics of ultrathin (HfO2)x(SiO2)1−x films by surface sol-gel method and reaction-anneal treatment

Hafnium oxide (HfO₂) films were deposited on Si substrates with a pre-grown oxide layer using hafnium chloride (HfCl₄) source by surface sol-gel process, then ultrathin (HfO₂)_x(SiO₂)_1−x films were fabricated due to the reaction of SiO₂ layer with HfO₂ under the appropriate reaction-anneal treatment. The observation of high-resolution transmission electron microscopy indicates that the ultrathin films show amorphous nature. X-ray photoelectron spectroscopy analyses reveal that surface sol-gel derived ultrathin films are Hf-Si-O alloy instead of HfO₂ and pre-grown SiO₂ layer, and the composition was Hf_0.52Si_0.48O₂ under 500 °C reaction-anneal. The lowest equivalent oxide thickness (EOT) value of 0.9 nm of film annealed at 500 °C has been obtained with small flatband voltage of −0.31 V. The experimental results indicate that a simple and feasible solution route to fabricate (HfO₂)_x(SiO₂)_1−x composite films has been developed by means of combination of surface sol-gel and reaction-anneal treatment.