Synthesis,structural characterization,and photoluminescence properties of Eu3+‐doped Mg3‐xEux(BO3)2 phosphor

Eu³⁺‐doped Mg_3‐xEu_x(BO₃)₂ (x = 0.000, 0.005, 0.010, 0.020, 0.050, and 0.100) phosphors were synthesized for the first time by solution combustion synthesis method, which is a fast synthesis method for obtaining nano‐sized borate powders. The optimization of the synthesis conditions of phosphor materials was performed by TG/DTA method. These phosphors were characterized by XRD, FTIR, SEM‐EDX, and photoluminescence, PL analysis. The XRD analysis exhibited that all of the prepared ceramic compounds have been crystallized in orthorhombic structure with space group Pnnm. Also, the influence of europium dopant ions on unit cell parameters of host material was analyzed using Jana2006 program and the crystalline size was determined by Debye‐Scherrer's formula. The luminescence properties of all Eu³⁺‐doped samples were investigated by excitation and emission spectra. The excitation spectra of Mg_3‐xEu_x(BO₃)₂ phosphors show characteristic peak at 420 nm in addition to other characteristic peaks of Eu³⁺ under emission at 613 nm. The emission spectra of Eu³⁺‐doped samples indicated most intensive red emission band dominated at 630 nm belonging to ⁵D₀→⁷F₂ magnetic dipole transition. Furthermore, the optimum or quenching concentration of Eu³⁺ ion has been determined as x = 0.010 showed the maximum emission intensity when it was excited at 394 nm.