采用单辊快速凝同法制备出厚约40μm的Mg_(80)Cu_(15)Y_5非品合金薄带,利用XRD、DSC、TEM和HRTEM研究了非品合金的非品形成能力和晶化行为,分析了品化对合金组织结构与性能的影响.结果表明:Mg_(80)Cu_(15)Y_5合金的过冷液态温度区间△T_x和约化玻璃转变温度T_(rg)分别为55K和0.58,表明其具有较强的非晶形成能力;该合金在退火温度高于473 K后发牛明显晶化,从非品基体中析出 Mg_2Cu、Cu_2Y和Mg晶体相;随着退火温度的升高,合金的硬度呈现出先升高后降低的变化趋势,这与纳米品体相颗粒的弥散析出、重溶及粗化有关.

Amorphous-forming Ability and Crystallization Behavior of Mg_(80)Cu_(15)Y_5 Alloy

Mg_(80)Cu_(15)Y_5 amorphous alloy ribbons with the thickness of approximately 40 μm were prepared by single-roll rapid solidification method.The amorphous-forming ability and crystallization behavior were studied using XRD,DSC,TEM and HRTEM.The effects of crystallization on microstructure and mechanical property of the alloy were analyzed.The results show Mg_(80)Cu_(15)Y_5 alloy has better amorphous-forming ability,the undercooled liquid region ΔT_x is 55 K and the reduced glass-transition temperature T_(rg)is 0.58.The remarkable crystallization of the alloy occurs after annealing above 473 K.Mg_2Cu,Cu_2Y and Mg crystalline phases are precipitated from the amorphous matrix.With the increase of annealing temperature,the microhardness of the alloy increases first and then decreases.The change in the microhardness of the alloy depends on the precipitation,re-melting and coarsening of the nano-crystalline particles.