Multiple melting in blends of poly(vinylidene fluoride) with isotactic poly(ethyl methacrylate)

Multiple melting phenomena have been studied in blends of poly(vinylidene fluoride) (PVF₂) with low molar mass isotactic poly(ethyl methacrylate) (it-PEMA). In all blends, as well as in pure PVF₂, a transition (T₁) was observed prior to the main melting point (T₂). T₁ is probably connected with the melting of secondarily-crystallized material. In addition to this, a high temperature melting endotherm (T₃) was observed, which could be ascribed completely to recrystallization of PVF₂. The highest transition (T₄) was caused by melting of the σ form of PVF₂. From Hoffman-Weeks plots—T₂ vs. crystallization temperature, T_c — it could be concluded that no thermody amic depression of the melting point of PVF₂ occurred in the blends. The stabilities of PVF₂ crystallites in the various blends were derived from the slopes of Hoffman-Weeks plots and were in good agreement with lamellar thicknesses found from SAXS measurements.