| Microstructure and Strain Hardening of a Friction Stir Welded High-Strength Al–Zn–Mg Alloy |
| |
| 作者姓名： | A.H.Feng D.L.Chen Z.Y.Ma W.Y.Ma R.J.Song |
| |
| 作者单位： | School of Materials Science and Engineering,Tongji University;State Key Laboratory of Advanced Welding Production Technology,School of Materials Science and Engineering,Harbin Institute of Technology;Department of Mechanical and Industrial Engineering,Ryerson University,Toronto,ON M5B 2K3,Canada;Shenyang National Laboratory for Materials Science,Institute of Metal Research,Chinese Academy of Sciences; |
| |
| 基金项目： | financially supported by Natural Sciences and Engineering Research Council of Canada （NSERC）; Premier’s Research Excellence Award （PREA）,NSERC-DAS Award,Canada Foundation for Innovation （CFI）; Ryerson Research Chair （RRC） program; National Outstanding Young Scientist Foundation of China （No.50525103）; Hundred Talents Program of the Chinese Academy of Sciences |
| |
| 摘 要： | Microstructural evolution and strain hardening behavior of a friction stir welded（FSWed） high-strength7075Al-T651 alloy were evaluated.The nugget zone was observed to consist of fine and equiaxed recrystallized grains with a low dislocation density and free of original precipitates,but containing uniformly distributed dispersoids.The strength,joint efficiency,and ductility of the FSWed joints increased with increasing welding speed.A joint efficiency of ＊91% was achieved at a welding speed of 400 mm/min and rotational rate of 800 r/min,while the ductility remained basically the same as that of the base metal.There was no obvious strain rate sensitivity observed in both base metal and welded joints.While both the base metal and FSWed joints exhibited stage III and IV hardening characteristics,the hardening capacity,strain hardening exponent,and strain hardening rate all increased after friction stir welding.
|
| 关 键 词： | 搅拌摩擦焊接 应变硬化 MG合金 组织演变 高强度 应变速率敏感性 焊接接头 基体金属 |
| 收稿时间： | 2013-11-24 |