Aqueous Processing and Stabilization of Manganese Zinc Ferrite Powders via a Passivation–Dispersion Approach

A dispersion scheme for aqueous processing of manganese zinc ferrite suspensions is presented. The addition of oxalic acid leads to the formation of a uniform negative charge on the surface such that a cationic polyelectrolyte, polyethyleneimine (PEI), adsorbs and provides electrosteric dispersion. At 0.5 w/w (weight percent with respect to the dry powder) oxalic acid addition, there is a relatively uniform negative surface charge (approximately ?30 mV) within the suspension pH range investigated (3–10), eliminating the isoelectric point (pH ～7.6) present for the as-received metal oxide powder. At the addition of 0.5 w/w PEI on an oxalate-treated surface, the surface charge is constant and positive (～20 mV) through a wide pH range, ～5–10. The resulting rheological data for passivation–dispersion of relatively high-solids manganese zinc ferrite suspensions (～80 wt%) demonstrate improved colloid stability with improved rheological properties. The resulting apparent viscosity and Bingham yield point is 0.01 Pa·s (12.0 cP) and 0.24 Pa (2.4 dynes/cm²), respectively. A sulfonated napthalene-based dispersant, typically used in industry, gives an apparent viscosity and Bingham yield point of 0.03 Pa·s (32 cP) and 3.1 Pa (31 dynes/cm²), respectively.