| Abstract: | The paper reports a new concept of planar‐tubular solid oxide fuel cell (PT‐SOFC). Emphasis is on the fabrication of the required complex configuration of Ni‐yttria‐stabilised zirconia (YSZ) porous anode support by tert‐butyl alcohol (TBA) based gelcasting, particularly the effects of solid loading, amounts of monomers and dispersant on the rheological behaviour of suspension, the shrinkage of a wet gelcast green body upon drying, and the properties of final sample after sintering at 1350 °C and reduction from NiO‐YSZ to Ni‐YSZ. The results show that the gelcasting is a powerful method for preparation of the required complex configuration anode support. The anode support resulted from an optimised suspension with the solid loading of 25 vol% has uniform microstructure with 37% porosity, bending strength of 44 MPa and conductivity of 300 S cm—1 at 700 °C, meeting the requirements for an anode support of SOFC. Based on the as‐prepared anode support, PT‐SOFC single cell of Ni‐YSZ/YSZ/LSCF has been fabricated by slurry coating and co‐sintering technique. The cell peak power density reaches 63, 106 and 141 mW cm—2 at 700, 750 and 800 °C, respectively, using hydrogen as fuel and ambient air as oxidant. |