Effect of annealing time on the exchange coupling interactions and microstructure of nanocomposite Pr7.5Dy1Fe71Co15Nb1B4.5 ribbons |
| |
Authors: | Xiaoqian Bao Yi Qiao Xuexu Gao Maocai Zhang Jie Zhu Shouzeng Zhou |
| |
Affiliation: | State Key Laboratory for Advanced Metals and Materials, University of Science and Technology Beijing, Beijing 100083, China |
| |
Abstract: | The influence of annealing time on the magnetic properties and microstructure of nanocomposite Pr7.5Dy1Fe71Co15Nb1B4.5 ribbons was systematically investigated by the methods of vibrating sample magnetometer (VSM), X-ray diffraction (XRD) and high resolution transmission electron microscopy (HRTEM). Interaction domains derived from strong exchange coupling interactions between hard and soft magnetic grains were imaged using magnetic force microscopy (MFM). Maximum remanence, intrinsic coercivity, and maximum energy product values were obtained in the ribbons annealed at 700°C for 15 min, which were composed of Pr2(Fe, Co)14B, -(Fe, Co), and slight Pr2(Fe, Co)17 phases. Although Jr Hd, and (BH)max decreased gradually with further increase of annealing time, it is emphasized that comparatively high Jr and Hci and (BH)max were obtained in a wide annealing time period of 15 to 360 min. The shape of initial magnetization curves and hysteresis loops change as a function of annealing time, indicating different magnetization reversal routes, which can be fully explained by the corresponding microstructure. |
| |
Keywords: | nanocomposite magnets exchange coupling interaction microstructure magnetization reversal |
本文献已被 维普 ScienceDirect 等数据库收录! |
|