| 焊接工艺对压铸镁合金CO2激光焊缝气孔率的影响 |
| |
| 引用本文： | 张婧,单际国,温鹏,任家烈.焊接工艺对压铸镁合金CO2激光焊缝气孔率的影响[J].焊接学报,2011,32(5):17-20,24. |
| |
| 作者姓名： | 张婧 单际国 温鹏 任家烈 |
| |
| 作者单位： | 1. 清华大学机械工程系,北京,100084
2. 清华大学机械工程系,北京,100084;清华大学先进成形制造教育部重点实验室,北京100084 |
| |
| 基金项目： | 国家自然科学基金资助项目，高等学校博士学科点专向科研基金项目 |
| |
| 摘 要： | 研究了激光功率和焊接速度等焊接工艺参数对两种不同含气量的压铸镁合金激光焊气孔倾向(以气孔率为表征)的影响规律,并对气孔的防止措施进行了探索.结果表明,含气量较高的2 mm厚压铸镁合金激光焊气孔倾向大于含气量较低的5 mm厚压铸镁合金.两种厚度的压铸镁合金激光焊缝气孔率总体上均随着激光功率的升高及焊接速度的降低而升高.对...
|
| 关 键 词： | 气孔 气孔防止 激光焊接 焊接工艺 压铸镁合金 |
| 收稿时间： | 2009/12/24 0:00:00 |
Effects of welding parameters on weld porosity during CO2 laser welding of die-cast magnesium alloys |
| |
| ZHANG Jing,SHAN Jiguo,WEN Peng and REN Jialie.Effects of welding parameters on weld porosity during CO2 laser welding of die-cast magnesium alloys[J].Transactions of The China Welding Institution,2011,32(5):17-20,24. |
| |
| Authors: | ZHANG Jing SHAN Jiguo WEN Peng and REN Jialie |
| |
| Affiliation: | Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China,Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China;Key Laboratory for Advanced Materials Processing Technology, The Ministry of Education, Tsinghua University, Beijing 100084, China,Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China;Key Laboratory for Advanced Materials Processing Technology, The Ministry of Education, Tsinghua University, Beijing 100084, China and Department of Mechanical Engineering, Tsinghua University, Beijing 100084, China |
| |
| Abstract: | The effects of welding parameters including laser power,welding speed,welding conditions on pore formation tendency(represented as porosity) during laser welding of die-cast magnesium alloys with two different gas contents were investigated,and the porosity prevention measures were also studied.It is shown that the pore formation tendency during laser welding of 2 mm thick die-cast magnesium alloys with higher gas content is greater than that of 5 mm thick die-cast magnesium alloys with lower gas content.As a whole,the porosity increases with the increase of laser power and the decrease of welding speed for both two thicknesses.For 5 mm thick die-cast magnesium alloys with lower gas content,low porosity weld bead can be obtained by both double sided welding and remelting after welding,and the porosity can reduce to 2.4% and 2.5%,respectively.However,for the 2 mm thick die-cast magnesium alloys,these porosity prevention measures are not effective. |
| |
| Keywords: | pore pore prevention laser welding welding parameters die-cast magnesium alloys |