| Abstract: | Compatibilizing effects of ethylene/propylene (EPR) diblock copolymers on the morphology and mechanical properties of immiscible blends produced from recycled low‐density polyethylene (PE‐LD) and high‐density polyethylene (PE‐HD) with 20 wt.‐% of recycled poly(propylene) (PP) were investigated. Two different EPR block copolymers which differ in ethylene monomer unit content were applied to act as interfacial agents. The morphology of the studied blends was observed by scanning‐ (SEM) and transmission electron microscopy (TEM). It was found that both EPR copolymers were efficient in reducing the size of the dispersed phase and improving adhesion between PE and PP phases. Addition of 10 wt.‐% of EPR caused the formation of the interfacial layer surrounding dispersed PP particles with the occurrence of PE‐LD lamellae interpenetration into the layer. Tensile properties (elongation at yield, yield stress, elongation at break, Young's modulus) and notched impact strength were measured as a function of blend composition and chemical structure of EPR. It was found that the EPR with a higher content of ethylene monomer units was a more efficient compatibilizer, especially for the modification of PE‐LD/PP 80/20 blend. Notched impact strength and ductility were greatly improved due to the morphological changes and increased interfacial adhesion as a result of the EPR localization between the phases. No significant improvements of mechanical properties for recycled PE‐HD/PP 80/20 blend were observed by the addition of selected block copolymers. |