Relationship between fracture toughness determined by surface crack in flexure and fracture resistance measured by indentation fracture for silicon nitride ceramics with various microstructures

The reliability of the Vickers indentation fracture (IF) method for various types of silicon nitride (Si₃N₄) ceramics was assessed by comparing the fracture resistance, K_R obtained from the IF test with the fracture toughness, K_Ic from the surface crack in flexure (SCF) technique in the same crack depth region. The K_R of a fine-grained and equiaxed Si₃N₄ matched with the K_Ic from the SCF test when Miyoshi's equation was used, while the K_Ic of a bearing-grade Si₃N₄ was found to lie between K_R values calculated with Niihara's equation (higher side) and Miyoshi's equations (lower side). In the case of coarse Si₃N₄ with elongated grains, the K_R determined using Niihara's equation gave the best fit with K_Ic. The inconsistent outcomes were explained by the probable mechanisms, indicating that the K_R from the IF test cannot be correlated directly with the K_Ic unless the effective crack length for the IF test was clarified.