Influence of rare-earth oxides on structure and crystallization properties of Bi2O3–B2O3 glass

Bi₂O₃·B₂O₃ glasses doped with rare-earth oxides (RE₂O₃) (RE³⁺ = La³⁺, Pr³⁺, Sm³⁺, Gd³⁺, Er³⁺ and Yb³⁺) were prepared by the melting–quenching method. The relationships between composition and properties were demonstrated by IR, DSC, XRD and SEM analysis. The results show that the network structure resembles that of undoped Bi₂O₃·B₂O₃ glass, composing of BO₃], BO₄] and BiO₆] units. RE₂O₃ stabilizes the glass structure as a modifier. Transition temperature (T_g) increases linearly with cationic field strength (CFS) of RE³⁺. La₂O₃, Pr₂O₃, Sm₂O₃ and Gd₂O₃ are benefit to promote the formation of BiBO₃ crystal. When Er₂O₃ and Yb₂O₃ are introduced, respectively, the main crystal phase changes to Bi₆B₁₀O₂₄. Transparent surface crystallized samples are obtained by reheating at 460–540 °C for 5 h. In this case, needle like BiBO₃ crystal or rare-earth-doped BiBO₃ crystal (Pr_xBi_1−xBO₃ and Gd_xBi_1−xBO₃) are observed, which is promising for non-linear optical application.