The MiniWiD-Coater. III. Effect of Application Temperature on the Dissolution Profile of Sustained-Release Theophylline Pellets Coated with Eudragit Rs 30 D
Authors:Peter C. Schmidt   Frank Niemann
Abstract:Theophylline pellets were coated with Eudragit RS 30 D in a miniature fluid-bed pan coater called MiniWiD developed recently. The dispersions were plasticized with varying amounts of triethyl citrate (TEC), dibutyl phthalate (DBP), and polyethylene glycol 6000 (PEG) and applied at different temperatures ranging from 25 to 45 °C. Theophylline release was tested by dissolution using the USP Apparatus 2 (paddle) in 0.1 N hydrochloric acid under sink conditions over 6 hours.

At a coating level of 4 % (0.7 mg/cm2) sustained-release profiles were obtained from dispersions plasticized with TEC or DBP. By reducing the amount of plasticizer from 20 to 10%, films with higher permeabilities were obtained. This effect was compensated by tempering the pellets at 50 deg;C for 24 hours. The coating temperature had little effect on the dissolution profiles of TEC-plasticized films and no effect on films with DBP.

Coatings plasticized with 20% PEG were applied at temperatures ranging from 25 to 45 °C. These films required a coating level of about 18 % (3.3 mg/cm2) to provide comparable sustained-release properties. In contrast to DBP and TEC, a strong influence of the coating temperature on the release rates was observed in which higher temperatures led to slower release rates. This behavior can be explained by the minimum film-forming temperature (MFT). Since PEG does not lower the MFT of Eudragit RS 30 D, the application of these films below the MFT of 45 °C is associated with a lower degree of film formation.
Keywords:
本文献已被 InformaWorld 等数据库收录!
设为首页 | 免责声明 | 关于勤云 | 加入收藏

Copyright©北京勤云科技发展有限公司  京ICP备09084417号