| 转筒干燥机裂纹失效分析 |
| |
| 引用本文： | 林萍,岳斌,等.转筒干燥机裂纹失效分析[J].化工机械,2001,28(3):157-159. |
| |
| 作者姓名： | 林萍 岳斌 |
| |
| 作者单位： | 化工部化工机械研究院 |
| |
| 摘 要： | 就复肥厂常规直接加热转筒干燥机焊缝上的裂纹进行了宏观及微观分析 ,找出裂纹形成的原因为应力腐蚀开裂 ,并提出修补措施
|
| 关 键 词： | 应力腐蚀开裂 干燥机 |
Crack failure analysis of cylinder dryers. |
| |
| Lin Ping,Yue Bin,Li Changxi,Liao Dongtai,Ma Pengju.Crack failure analysis of cylinder dryers.[J].Chemical Engineering & Machinery,2001,28(3):157-159. |
| |
| Authors: | Lin Ping Yue Bin Li Changxi Liao Dongtai Ma Pengju |
| |
| Abstract: | A macro analysis and a micro analysis was made for the weld seam cracks on the cylinder dryers in a compound fertilizer plant,and it was found out that the cause was stress corrosion cracking,and some repair methods were proposed. |
| |
| Keywords: | Stress Corrosion Cracking Dryer |