| Oxidation of Al2O3-30%TiCN-0.2%Y2O3 Composite | |
| 引用本文： | 李喜坤 邱关明 修稚萌 孙旭东 严长浩 代少俊. Oxidation of Al2O3-30%TiCN-0.2%Y2O3 Composite[J]. 中国稀土学报(英文版), 2005, 23(3): 276-279 |
| 作者姓名： | 李喜坤 邱关明 修稚萌 孙旭东 严长浩 代少俊 |
| 作者单位： | Shenyang University of Science and Techology，Shenyang 110168，China，Nanjing University of Technoloy，Nanjing 210009，China，Nanjing University of Technoloy，Nanjing 210009，China，Changchun University of Science and Technology，Changchun 130022，China，School of Materials and Metallurgy Northeastern University，Shenyang 110004，China，School of Materials and Metallurgy Northeastern University，Shenyang 110004，China，Nanjing University of Technoloy，Nanjing 210009，China，Nanjing University of Technoloy，Nanjing 210009，China |
| 基金项目： | theNationalNaturalScienceFoundationofChina (5 0 172 0 10 )andtheNaturalScienceFoundationofLiaoningProvince (2 0 0 110 10 0 2 ) |
| 摘 要： | Thecuttingtoolmaterialshavegoodoxidationre sistance ,buttheyareoxidizedathightemperature(about 10 0 0℃ )duringoperation .Themechanicalpropertyofthecuttingtoolmaterialswillbechange d[1,2 ] .Therefore ,researchonoxidationbehaviorofcuttingtoolsmaterialsathi… |
| 关 键 词： | Al2O3 TiCN Y2O3 稀土 氧化反应 弯曲强度 温度 切割材料 |
Oxidation of Al2O3-30%TiCN-0.2%Y2O3 Composite |
|
| Li Xikun,QIU Guanming,Xiu Zhimeng,SUN Xudong,Yan Changhao,Dai Shaojun. Oxidation of Al2O3-30%TiCN-0.2%Y2O3 Composite[J]. Journal of Rare Earths, 2005, 23(3): 276-279 | |
| Authors: | Li Xikun QIU Guanming Xiu Zhimeng SUN Xudong Yan Changhao Dai Shaojun |
| Abstract: | The oxidation behavior of Al2O3-30%TiCN-0.2%Y2O3 composite and its effect on high temperature bending strength was studied. The result indicates that the mass gain during static oxidation of the material under normal atmosphere follows the parabolic law. Oxide increases with increasing temperature and prolonging time. It has good oxidation resistance. The product of oxidation of the material is TiO2. Therefore, the volume of the material expands. The oxide film is destroyed because residual stress inside the oxide film is released. Proper oxidation is beneficial to the improvement of bending strength of Al2O3-30%TiCN-0.2%Y2O3 composite. The strength increase is up to 4.5%. |
| Keywords: | composite Al2O3-30%TiCN-0.2%Y2O3 oxidation behavior bend strength parabolic law residual stress rare earths |
| 本文献已被 CNKI 维普 万方数据 等数据库收录！ | |