Blends of head-to-head polystyrene with poly(2,6-dimethyl-1,4-phenylene oxide)

Blends of head-to-head polystyrene and poly(2,6-dimethyl-1,4-phenylene oxide) were prepared and found to be miscible as judged by a single T_g. The measurements were carried out by d.s.c. and dilatometry. At high concentrations of PPO (> 80%) the mixture is on the threshold of incompatibility as indicated by the increase of the width of the transition step increase by d.s.c. and the increase of the free volume as calculated from dilatometric data. The thermal stability studies of head-to-head polystyrene-(HH-PS)-poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) blends by thermal volatilization analysis show two decomposition processes in the temperature range characteristic for both homopolymers. The temperature of the maximum rate of decomposition for PPO in the blend is slightly shifted towards lower temperatures as compared with pure PPO. This can be explained by assuming that the PPO degradation is induced by radicals formed during the decomposition of HH-PS.