Effects of processing parameters on microstructure of semi-solid magnesium alloy |
| |
摘 要: | In this paper, the effects of pouring temperature of magnesium melt, preheating temperature of the barrel of the screw mixer, and shear rate on the solidified microstructures of semi-solid slurry were investigated by a mechanical stirring semi-solid process. The appropriate processing parameters of slurry preparation were obtained, and the mold filling ability of semi-solid slurry for thin-walled casting was examined. Results indicate that the solid volume fraction of non-dendritic microstructure increases with a decrease in pouring temperature of magnesium melt and the barrel preheating temperature of the screw mixer. Also the grain size of primary α-phase is reduced. Furthermore, the solid volume fraction of semi-solid nondendritic structure decreases with an increase of shear rate. The fine and round granular microstructure with 30~50 μm in size of semi-solid AZ91D magnesium alloy was presented. Finally, a 1.0 mm thin-walled casting with a clear contour and good soundness was successfully made by semi-solid rheo-diecasting.
|
Effects of processing parameters on microstructure of semi-solid magnesium alloy |
| |
Authors: | Shusen WU Dongnan LI Youwu MAO Zehui XIAO Jirong LUO |
| |
Abstract: | In this paper, the effects of pouring temperature of magnesium melt, preheating temperature of the barrel of the screw mixer, and shear rate on the solidified microstructures of semi-solid slurry were investigated by a mechanical stirring semi-solid process. The appropriate processing parameters of slurry preparation were obtained, and the mold filling ability of semi-solid slurry for thin-walled casting was examined. Results indicate that the solid volume fraction of non-dendritic microstructure increases with a decrease in pouring temperature of magnesium melt and the barrel preheating temperature of the screw mixer. Also the grain size of primary α-phase is reduced. Furthermore, the solid volume fraction of semi-solid nondendritic structure decreases with an increase of shear rate. The fine and round granular microstructure with 30 ~50 μm in size of semi-solid AZ91D magnesium alloy was presented. Finally, a 1.0 mm thin-walled casting with a clear contour and good soundness was successfully made by semi-solid rheo-diecasting. |
| |
Keywords: | semi-solid metal magnesium alloy rheocasting slurry microstructure |
本文献已被 万方数据 等数据库收录! |
|