Microstructure, Chemical and Phase Composition of Chromium Silicide Diffusion Coatings on Carbon Steels

The microstructure, chemical and phase composition of chromium silicide diffusion coatings on steels 20, 45, U8, and U10 are studied. It is established that the phases Cr²³C⁶ and Cr⁷C³ with a silicon content in them of up to 0.25 at.% form at the surface of chromium silicide coatings. The maximum silicon content at 7% in steels 20 and 45 is observed beneath the carbide layer at a depth of 40–50 µm, but for steel U10 it is 1.9% at the carbide layer-matrix boundary. It is shown that the corrosion resistance of chromium silicide diffusion coatings increases markedly compared with uncoated specimens: by a factor of 15–30 depending on the acid used (H₂SO₄, HCl, H₃PO₄, HNO₃, CH₃COOH). There is also an increase in the cavitation resistance of articles with chromium silicide coatings in water and 3% NaCl solution.__________Translated from Poroshkovaya Metallurgiya, Nos. 1–2(441), pp. 23–30, January–February, 2005.