Processing and Properties of Textured Potassium Sodium Niobate [K,Na]NbO3 Ceramic Ribbons by Alginate Gelation Method

Random and <001> textured potassium sodium niobate – K,Na]NbO₃ (KNN) ceramics with 1 mole% CuO sintering aid were fabricated in ribbon form through a combination of novel alginate gelation process and templated grain growth methods using platelike sodium niobate ‐ NaNbO₃ (NN) template particles. The platelike NN template particles were prepared by a two‐step molten salt synthesis method. Ribbons were drawn from alginate‐based slurries without or with 10 wt% NN template particles using 50 mm long slit nozzle with a rectangular orifice of 10 mm × 1 mm. Development of crystallographic texture as a result of varying sintering time and temperature was evaluated through the calculation of the degree of orientation as measured by the Lotgering factor (?₍₀₀₁₎) and an ?₍₀₀₁₎ of 0.81 was achieved. The electrical properties of textured ribbons were evaluated with polarization and strain versus electric field measurements.