The performances of higher alcohol synthesis over nickel modified K2CO3/MoS2 catalyst

Ni modified K₂CO₃/MoS₂ catalyst was prepared and the performance of higher alcohol synthesis catalyst was investigated under the conditions: T = 280–340 °C, H₂/CO (molar radio) = 2.0, GHSV = 3000 h^− 1, and P = 10.0 MPa. Compared with conventional K₂CO₃/MoS₂ catalyst, Ni/K₂CO₃/MoS₂ catalyst showed higher activity and higher selectivity to C₂⁺OH. The optimum temperature range was 320–340 °C and the maximum space-time yield (STY) of alcohol 0.30 g/ml h was obtained at 320 °C. The selectivity to hydrocarbons over Ni/K₂CO₃/MoS₂ was higher, however, it was close to that of K₂CO₃/MoS₂ catalyst as the temperature increased. The results indicated that nickel was an efficient promoter to improve the activity and selectivity of K₂CO₃/MoS₂ catalyst.