| Effect of Thickness on the Structure and Tribological Properties of MoSx Coating |
| |
| 作者姓名： | JihuiWANG E.Wieers |
| |
| 作者单位： | [1]SchoolofMaterialsScienceandEngineering,TianjingUniversityTianjin300072,China [2]InstituteforMaterialsResearch,LimburgUniversityCentrum,B－3590Diepenbeek,Belgium |
| |
| 基金项目： | This research is a part of an Eureka project funded by the Flemish government (Lubrimat 960235), a Belgium-China interna-tional scientific and technological co-operation project supported by the Flemish government and the China government (project BIL 96 |
| |
| 摘 要： | MoSx coatings were prepared by bipolar-pulse DC unbalanced magnetron-sputtering system with the variation of coating thickness at different Ar pressures.The composition and surface morphology were determined by using energy dispersive X-ray and scanning electron microscopy;the structural characterization was analyzed by X-ray diffraction.The friction and wear properties were investigated by fretting tests in air with less than 10% and 50% relative humidity.At 0.40 Pa pressure,(002) basal plane orientation was formed throughout the coatings.At 0.88 Pa and 1.60 Pa pressures,(002) basal plane orientation was only noticed in the first stage of coating growth(around 0.20 μm in thickness), and then edge orientations with their basal planes perpendicular to the surface would be evolved in the coatings.Humidity has a minor influence on the coatings that have(002) basal plane orientation,whereas the tribological properties of MoSx coatings with edge orientations are greatly affected by humidity.The mechanisms of coating growth and friction and wear processes are discussed.
|
| 关 键 词： | 硫化钼涂层 厚度 结构 性质 金属 X射线衍射 表面涂层 |
| 收稿时间： | 2001-07-30 |
Effect of Thickness on the Structure and Tribological Properties of MoSx Coating |
| |
| Jihui WANG,E.Wieers,L.M.Stals,J.P.Celis.Effect of Thickness on the Structure and Tribological Properties of MoSx Coating[J].Journal of Materials Science & Technology,2002,18(4):361-364. |
| |
| Authors: | Jihui WANG EWieers LMStals JPCelis |
| |
| Affiliation: | School of Materials Science and Engineering, Tianjin University, Tianjin 300072, China ... |
| |
| Abstract: | MoSx coatings were prepared by bipolar-pulse DC unbalanced magnetron-sputtering system with the variation of coating thickness at different Ar pressures. The composition and surface morphology were determined by using energy dispersive X-ray and scanning electron microscopy; the structural characterisation was analyzed by X-ray diffraction. The friction and wear properties were investigated by fretting tests in air with less than 10% and 50%relative humidity. At 0.40 Pa pressure, (002) basal plane orientation was formed throughout the coatings. At 0.88Pa and 1.60 Pa pressures, (002) basal plane orientation was only noticed in the first stage of coating growth (around 0.20 μm in thickness), and then edge orientations with their basal planes perpendicular to the surface would be evolved in the coatings. Humidity has a minor influence on the coatings that have (002) basal plane orientation,whereas the tribological properties of MoSs coatings with edge orientations are greatly affected by humidity. The mechanisms of coating growth and friction and wear processes are discussed. |
| |
| Keywords: | MoSx coating Magnetron sputtering Friction Wear |